1) cast iron pressing quenching
铸铁夹压淬火
2) ADI
等温淬火球墨铸铁
1.
The Investigation on Surface Heat Treatment Process of ADI;
等温淬火球墨铸铁表面热处理工艺的研究
2.
Two austempered ductile irons (ADIs) specimens, with Bi and without Bi, were prepared by heating at 880℃for 60 min and austempering at 280℃for 120 min.
对有Bi和无Bi 2种成分的等温淬火球墨铸铁进行了组织、微区成分定量分析和机械性能、耐磨性能的对比实验研究。
3.
Four kinds of polycrystalline cubic boron nitride(PCBN) compact tools were used to cut the austempered ductile iron(ADI) in the experiment for the purpose of getting the curves of cutting force,friction force and friction coefficient with the change of cutting speed.
通过用四种不同聚晶立方氮化硼(PCBN)复合刀具切削等温淬火球墨铸铁(ADI)进行切削力试验,得出了不同刀具切削力、摩擦力以及摩擦因数随切削速度的变化曲线。
3) austempered ductile iron(ADI)
等温淬火球墨铸铁(ADI)
4) AMI iron
等温淬火球墨可锻铸铁
5) induction hardening of pearlitic malleable iron
可锻铸铁感应淬火
6) austempered ductile iron
等温淬火球墨铸铁
1.
In order to produce high toughness austempered ductile iron(ADI),the influence of chemical composition and heat treatment was studied.
为了稳定某高韧性等温淬火球墨铸铁(ADI)铸件的生产,对其进行了化学成分设计,加入铜、钼、镍等元素进行适当的合金化,铸造球铁毛坯,然后采用在880~920℃奥氏体化、350~370℃等温淬火工艺进行热处理,对其性能进行了测试。
2.
The results obtained show that the fatiguelife of austempered ductile iron increases with the increase of ductility and decrease of tensile strength.
结果表明，等温淬火球墨铸铁的疲劳寿命随塑性的上升与强度的下降而增高。
补充资料：球墨铸铁
析出的石墨呈球形的铸铁。球状石墨对金属基体的割裂作用比片状石墨小，使铸铁的强度达到基体组织强度的70～90％，抗拉强度可达120kgf/mm2，并且具有良好的韧性。球墨铸铁除铁外的化学成分通常为：含碳量3.6～3.8％，含硅量2.0～3.0％，含锰、磷、硫总量不超过1.5％和适量的稀土、镁等球化剂。
球墨铸铁生产工艺简单，铸造性能比铸钢好（但比灰口铸铁差），成本低，因此，被广泛用来制作受力复杂，对强度和韧性以及耐磨性要求较高的零件，如曲轴、齿轮、高压缸、汽车底盘零件等。20世纪70年代全世界的球墨铸铁管的年产量达数百万吨。中国古代铸铁中亦有球状石墨的组织（见冶金史）。
球墨铸铁生产工艺简单，铸造性能比铸钢好（但比灰口铸铁差），成本低，因此，被广泛用来制作受力复杂，对强度和韧性以及耐磨性要求较高的零件，如曲轴、齿轮、高压缸、汽车底盘零件等。20世纪70年代全世界的球墨铸铁管的年产量达数百万吨。中国古代铸铁中亦有球状石墨的组织（见冶金史）。