2) aging properties
老化特性
1.
The species and properties of synthetic fibers used in concrete are introduced and compared, then the functions,mechanism and aging properties of synthetic fibers reinforced concrete are discussed further.
综述了合成纤维在建筑行业中混凝土建材上的应用,并系统介绍了适用于混凝土建材中的常用合成纤维的种类及其性能特点,合成纤维对混凝土抗裂、抗渗、增韧、抗冲击等的作用及机理,以及合成纤维在混凝土基体中的老化特性。
3) heat aging property
热老化性能
1.
5% of the mass of precipitated silica,was added into the MVQ together with SiO2 at the same time,and the results show that the anti-heat aging property and t.
5%的甲基乙烯基硅油可改善硫化成型后的LDPE/MVQ-SiO2并用胶的耐热老化性能和拉伸性能,硬度和扯断伸长率基本不变,但耐撕裂强度有所下降;制备LDPE/MVQ-SiO2并用胶时,加入质量为LDPE质量的1%的抗氧剂,可防止并用胶胶料在第2段硫化过程中,由于LDPE热降解所引起的材料性能劣化;在抗氧剂和硫化剂共同作用下,并用胶胶料合适的第2段硫化条件是200℃,硫化2 h。
2.
The results showed that the heat aging property of vulcanizates,the H pull-out force of aged ply compound and the performance of finished product improved without adverse effect on the physical properties of vulcanizates by adding 1 phr FHD-60 to carcass ply and inner tube compounds of bias tire respectively.
结果表明,在斜交轮胎帘布胶和内胎胶中加入1份防老剂FHD-60,对硫化胶的物理性能无不良影响,可提高硫化胶的耐热老化性能、帘布胶老化后的H抽出力及成品性能。
5) non aging property
不老化特性
6) hot air aging property
热空气老化性能
1.
The effects of conventional reinforcing agents(carbon black and silica),montmorillonite(original and OMMT)and salts of unsaturated carboxylic acids(zinc methacrylate and magnesium methacrylate)on the physical properties and hot air aging property of HNBR compounds were investigated,and the microstructure was characterized by SEM,TEM and TGA.
试验研究常规补强剂(炭黑、白炭黑)、蒙脱土(原土、有机蒙脱土)和不饱和羧酸盐(甲基丙烯酸锌、甲基丙烯酸镁)三类补强剂对氢化丁腈橡胶胶料物理性能和热空气老化性能的影响,并用扫描电镜、透射电镜和热重分析等方法对其微观结构进行表征。
补充资料：热老化
分子式：
分子量：
CAS号：
性质：聚合物受热而性能变劣的过程。大多数聚合物的热老化是由光、氧和受热共同作用所引起的降解和交联反应。降解会引起变软、发粘；交联则使材料变硬、发脆。例如顺丁橡胶的热老化会使其交联、变硬而失去弹性。
分子量：
CAS号：
性质：聚合物受热而性能变劣的过程。大多数聚合物的热老化是由光、氧和受热共同作用所引起的降解和交联反应。降解会引起变软、发粘；交联则使材料变硬、发脆。例如顺丁橡胶的热老化会使其交联、变硬而失去弹性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条