3) heat aging property
热老化性能
1.
5% of the mass of precipitated silica,was added into the MVQ together with SiO2 at the same time,and the results show that the anti-heat aging property and t.
5%的甲基乙烯基硅油可改善硫化成型后的LDPE/MVQ-SiO2并用胶的耐热老化性能和拉伸性能,硬度和扯断伸长率基本不变,但耐撕裂强度有所下降;制备LDPE/MVQ-SiO2并用胶时,加入质量为LDPE质量的1%的抗氧剂,可防止并用胶胶料在第2段硫化过程中,由于LDPE热降解所引起的材料性能劣化;在抗氧剂和硫化剂共同作用下,并用胶胶料合适的第2段硫化条件是200℃,硫化2 h。
2.
The results showed that the heat aging property of vulcanizates,the H pull-out force of aged ply compound and the performance of finished product improved without adverse effect on the physical properties of vulcanizates by adding 1 phr FHD-60 to carcass ply and inner tube compounds of bias tire respectively.
结果表明,在斜交轮胎帘布胶和内胎胶中加入1份防老剂FHD-60,对硫化胶的物理性能无不良影响,可提高硫化胶的耐热老化性能、帘布胶老化后的H抽出力及成品性能。
4) ageing stability
热氧老化稳定性
1.
The ageing stability of the blends of ENR/NBR was in vestigated by employing the differential Scanning Calorimeter(DSC), tensile tester and ageing oven.
采用差示扫描量热计,强力试验机,老化烘箱等设备研究环氧化天然胶(ENR)/丁腈胶(NBR)共混物的耐热氧老化稳定性。
5) ozone aging properties
臭氧老化性能
6) hot air aging property
热空气老化性能
1.
The effects of conventional reinforcing agents(carbon black and silica),montmorillonite(original and OMMT)and salts of unsaturated carboxylic acids(zinc methacrylate and magnesium methacrylate)on the physical properties and hot air aging property of HNBR compounds were investigated,and the microstructure was characterized by SEM,TEM and TGA.
试验研究常规补强剂(炭黑、白炭黑)、蒙脱土(原土、有机蒙脱土)和不饱和羧酸盐(甲基丙烯酸锌、甲基丙烯酸镁)三类补强剂对氢化丁腈橡胶胶料物理性能和热空气老化性能的影响,并用扫描电镜、透射电镜和热重分析等方法对其微观结构进行表征。
补充资料：氧压热老化
分子式：
CAS号：
性质：橡胶类材料在一定的纯氧压力和高温作用下产生的变化。试验时，在能经受加热加压的容器内悬挂试样，于70℃±1℃温度下，将容器中的空气全部用氧置换，并加压到2.1MPa±0.1MPa。根据材料的老化速度选择老化时间，常规时间为24、48、168和336h。老化结束测定试样老化前后拉伸强度和伸长率的变化百分率。通过测定氧化反应的吸氧量，以吸氧诱导期的长短来判断材料的耐热氧老化性能。
CAS号：
性质：橡胶类材料在一定的纯氧压力和高温作用下产生的变化。试验时，在能经受加热加压的容器内悬挂试样，于70℃±1℃温度下，将容器中的空气全部用氧置换，并加压到2.1MPa±0.1MPa。根据材料的老化速度选择老化时间，常规时间为24、48、168和336h。老化结束测定试样老化前后拉伸强度和伸长率的变化百分率。通过测定氧化反应的吸氧量，以吸氧诱导期的长短来判断材料的耐热氧老化性能。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条