1) alumina matrix ceramic coatings
Al2O3基陶瓷涂层
1.
The protective alumina matrix ceramic coatings are prepared on stainless steel by thermochemical reaction method.
采用热化学反应法在Q235钢表面制备具有保护性的Al2O3基陶瓷涂层。
2) Al2O3 ceramic coatings
Al2O3陶瓷涂层
1.
According to the fact that Al2O3 ceramic coatings have low adhesion strength and high porosity, two kinds of Al2O3 gradient ceramic coatings using NiAl intermetallic compound and Cu powders as transitive materials respectively were prepared by plasma spraying, and the microstructure of gradient coatings was observed, and the adhesion strength and porosity of the coatings were tested and analyzed.
针对Al2O3陶瓷涂层结合强度低、孔隙率高的实际,选择NiAl金属间化合物和金属铜粉作为过渡材料,利用等离子喷涂制备Al2O3梯度陶瓷涂层,并对梯度涂层进行组织形貌观察,测试结合强度和孔隙率。
3) Al2O3-hased composite ceramic coating
Al2O3基复合陶瓷涂层
4) nano Al2O3 ceramic coating
纳米Al2O3基陶瓷涂层
5) Al_2O_3-TiO_2 ceramic coating
Al2O3-TiO2陶瓷涂层
6) Al 2O 3 coated engineering ceramics
Al2O3涂层工程陶瓷
补充资料：Al
元素符号： al 英文名： aluminum 中文名： 铝
相对原子质量： 26.9815 常见化合价： +3 电负性： 1.61
外围电子排布： 3s2 3p1 核外电子排布： 2,8,3
同位素及放射线： al-26[730000y] *al-27 al-28[2.3m]
电子亲合和能： 48 kj·mol-1
第一电离能： 577.6 kj·mol-1 第二电离能： 1817 kj·mol-1 第三电离能： 2745 kj·mol-1
单质密度： 2.702 g/cm3 单质熔点： 660.37 ℃ 单质沸点： 2467 ℃
原子半径： 1.82 埃 离子半径： 0.51(+3) 埃 共价半径： 1.18 埃
常见化合物： al2o3 alcl3 al2s3 naalo2 al2(so4)3 al(oh)3
发现人： 厄斯泰德、维勒 时间： 1825 地点： 丹麦
名称由来：
拉丁文：alumen， aluminis（铝）。
元素描述：
柔软轻质的银白色金属，在地壳中含量第三。
元素来源：
自然界完全没有铝单质存在。可以电解铝土(al2o3)制取铝。
元素用途：
上自飞机下到易拉罐应用广泛。因为纯铝太柔软，所以要加入不到1%的硅或铁以加大其硬度和强度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条