1) alite-rich Portland cement
高阿利特水泥
1.
The effect of slag,fly ash,and calcined shale on setting time,compressive strength,resistivity,composition and microstructure of hydrated product of alite-rich Portland cement were studied.
研究了矿渣、粉煤灰和烧页岩单掺及复掺对高阿利特水泥凝结时间、抗压强度、电阻率、水化产物组成及微观结构的影响。
2) Alite blastfurnace-slag cement
阿利特高炉矿渣水泥
3) high alite content clinker
高阿利特水泥熟料
1.
The different kinds of low temperature formed minerals were selected as raw materials to prepare high alite content clinker.
针对高阿利特水泥熟料矿物体系,采用掺加不同低温矿物配料的方法,研究了不同配料方式对C3S形成的影响。
4) alinite cement
阿利尼特水泥
1.
The hydraulic properties,mechanical properties and energy-saving characteristic of alinite cement are sum- rnarized.
阿利尼特水泥是一种节能水泥。
2.
The influence of gypsum on the forming of early hydrated product of new white alinite cement added gypsum was studied by means of DTA, XRD and SEM .
利用DTA,XRD,SEM等方法,研究了石膏对新型白色阿利尼特水泥的早期水化产物形成的影响。
3.
Municipal solid waste incinerator (MSWI) fly ash was successfully used as raw material in sintering alinite cement clinker in the laboratory.
以城市垃圾焚烧飞灰(以下简称焚烧飞灰)为主要原料,在实验室电炉里成功烧成了阿利尼特水泥熟料,分析了熟料烧成所需适宜的生料组成和最佳煅烧温度,并研究了石膏掺量对阿利尼特水泥强度影响,以及阿利尼特水泥的标准稠度用水量和凝结时间。
5) high-activity alite-sulphoaluminate cement
高活性阿利特硫铝酸盐水泥
1.
Based on those properties of the clinker, a kind of compound cement, high-activity alite-sulphoaluminate cement (HAASC) was prescribed.
在此基础上,提出了高活性阿利特硫铝酸盐水泥方案。
6) High belite cement
高贝利特水泥
1.
Effect of fly ash on the workability,strength and hydration heat of high belite cement and concrete.;
粉煤灰对高贝利特水泥和混凝土的工作性、强度及水化热的影响
2.
This paper briefly introduces the production and the characteristic of high Belite cement, and discusses the main reason of its good workability, high long-term strength and perfect durability,meanwhile,also discusses its adaptability to the climate of Hainan.
简要介绍了高贝利特水泥的生产及其特性 ,讨论了高贝利特水泥具有工作性好、长期强度高和耐久性好的主要原因及其与海南气候的适应性 。
3.
Compatibility of high belite cement, Portland cement and ordinary Portland cement with superplasticizer and effect of mineral admixtures on the compatibility of high belite cement have been studied with the test of the workability of concrete as reaffirmation.
研究了高效减水剂与高贝利特水泥、硅酸盐水泥、普通硅酸盐水泥的相容性以及矿物掺合料对高贝利特水泥相容性的影响 ,并以混凝土工作性指标进行验证。
补充资料：才利特
分子式：
CAS号：
性质：又称C矿。硅酸盐水泥熟料中存在于阿利特和贝利特之间的铁铝酸盐晶体。是6CaO·2Al2O3·Fe2O3-6CaO·Al2O3·2Fe2O3之间的一系列固溶体。也有认为组成是8CaO·3Al2O3·Fe2O3-2CaO·Fe2O3之间的连续固溶体。平均组成接近于铁铝酸四钙(4CaO·Al2O3·Fe2O3)。属斜方晶系，常呈圆粒状和棱柱状。密度3.77g/cm3。偏光镜下，具有从浅褐色到深褐色的多色性。负光性。二轴晶晶体折射率ng=2.04(Li)，nm=2.01(Li)，np=1.96(Li)，双折射率ng-np=0.03。反光镜下反射能力强，呈亮白色，故通常称白色中间相。具有较好的抗冲击性能和抗硫酸盐性能。
CAS号：
性质：又称C矿。硅酸盐水泥熟料中存在于阿利特和贝利特之间的铁铝酸盐晶体。是6CaO·2Al2O3·Fe2O3-6CaO·Al2O3·2Fe2O3之间的一系列固溶体。也有认为组成是8CaO·3Al2O3·Fe2O3-2CaO·Fe2O3之间的连续固溶体。平均组成接近于铁铝酸四钙(4CaO·Al2O3·Fe2O3)。属斜方晶系，常呈圆粒状和棱柱状。密度3.77g/cm3。偏光镜下，具有从浅褐色到深褐色的多色性。负光性。二轴晶晶体折射率ng=2.04(Li)，nm=2.01(Li)，np=1.96(Li)，双折射率ng-np=0.03。反光镜下反射能力强，呈亮白色，故通常称白色中间相。具有较好的抗冲击性能和抗硫酸盐性能。