1) alite-sulphoaluminate cement
阿利特-硫铝酸盐水泥
1.
Study of compatibility of superplasticizers with alite-sulphoaluminate cement;
减水剂对阿利特-硫铝酸盐水泥适应性的研究
2.
Effect of mineral composition on adaptability of alite-sulphoaluminate cement with superplasticizer
矿物组成对阿利特-硫铝酸盐水泥与减水剂适应性的影响
3.
The formula of modulus value of alite-sulphoaluminate cement clinker was determined theoretically depending on its mineral composition and requirement for production control.
根据阿利特-硫铝酸盐水泥熟料的矿物组成及生产控制要求,从理论上推导出其率值计算公式。
2) high-activity alite-sulphoaluminate cement
高活性阿利特硫铝酸盐水泥
1.
Based on those properties of the clinker, a kind of compound cement, high-activity alite-sulphoaluminate cement (HAASC) was prescribed.
在此基础上,提出了高活性阿利特硫铝酸盐水泥方案。
3) alite-sulphoaluminate cement clinker
阿利特-硫铝酸盐水泥熟料
1.
Influence of MnO_2 on the burnability and mineral formation of alite-sulphoaluminate cement clinker;
MnO_2对阿利特-硫铝酸盐水泥熟料煅烧及矿物形成的影响
2.
Effect of TiO_2 on burnability and mineral formation of alite-sulphoaluminate cement clinker;
TiO_2对阿利特-硫铝酸盐水泥熟料煅烧及矿物形成影响的研究
4) alite-barium calcium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The effects of the composition of clinker minerals,gypsum content and environment temperature on the slurry rheological and dry shrinkage properties of alite-barium calcium sulphoaluminate cement were studied.
结果表明:阿利特—硫铝酸钡钙水泥的新拌浆体属于Bingham型流体,水泥浆体的屈服应力和黏度受熟料中硫铝酸钡钙矿物含量变化的影响较大,随石膏掺量的增加和环境温度的增高而减小;阿利特-硫铝酸钡钙水泥具有一定的微膨胀性能,其砂浆的干缩性能优于硅酸盐水泥砂浆。
2.
Experimental results show that when the slag content is 10% the compressive strength of alite-barium calcium sulphoaluminate cement reachs 44.
研究矿渣掺量对阿利特-硫铝酸钡钙水泥性能的影响,当质量分数掺量为10%时,阿利特-硫铝酸钡钙水泥3 d、28 d的强度分别达到44。
3.
The drying shrinkage and mechanical property of alite-barium calcium sulphoaluminate cement (SABC) mortars were investigated by contrasting with Portland cement mortars.
通过与硅酸盐水泥(portland cement,PC)对比,研究了阿利特-硫铝酸钡钙水泥(alite-barium calcium sulphoaluminate cement,SABC)砂浆的力学性能和干缩性能。
5) alite-calcium barium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The influence of different contents of slag,fly ash and zeolite powers on the strength of alite-calcium barium sulphoaluminate cement mortar is investigated,and the reaction mechanism is discussed.
研究不同掺量的矿渣、粉煤灰和沸石粉对阿利特-硫铝酸钡钙水泥砂浆强度的影响规律,并对其反应机理进行探讨。
2.
Effects of slag on the structure and properties of cement pastes were studied by determining the setting time, the mechanical property and pore structure of hardened Alite-Calcium Barium Sulphoaluminate cement pastes, and using scanning electron microscopy and DTA-TG.
通过对水泥浆体凝结性能、力学性能和孔结构的测定,结合扫描电镜分析和差热-热重分析,研究了矿渣掺量对阿利特-硫铝酸钡钙水泥浆体硬化浆体结构和性能的影响。
6) Alite-C2.75B1.25A3S cement
阿利特-硫铝酸钡钙水泥
1.
Compared with Portland cement concrete,the impermeability of Alite-C2.
在与相同配合比的普通硅酸盐水泥混凝土的对比试验中,采用抗渗试验和孔结构分析的方法,研究了阿利特-硫铝酸钡钙水泥混凝土的抗渗性能与水灰比的关系。
补充资料：铝酸盐水泥
分子式：
CAS号：
性质：熟料矿物以铝酸盐为主的水泥。其中主要的品种为矾土水泥，又称高铝水泥。矾土水泥加水后，一天强度可达其标号的90％，可用于紧急抢修工程。矾土水泥不宜用于常温尤其是潮湿环境，更不能用蒸汽养护，严禁电热法施工。矾土水泥水化热大，放热迅速，适于浇筑很薄的构件和寒冷地区施工。在低温和干燥环境下，低水灰比矾土水泥有很强的抗硫酸盐腐蚀的能力。矾土水泥耐火性好，使用不同的耐火骨料时，可用于900～1000℃和1300～1500℃甚至1400～1600℃温度下的耐火混凝土。矾土水泥不得与硅酸盐水泥及其他能析出Ca(OH)2的胶凝材料和含CaO的物质混合使用，否则将引起迅速凝结和强度急剧下降。见高铝水泥
CAS号：
性质：熟料矿物以铝酸盐为主的水泥。其中主要的品种为矾土水泥，又称高铝水泥。矾土水泥加水后，一天强度可达其标号的90％，可用于紧急抢修工程。矾土水泥不宜用于常温尤其是潮湿环境，更不能用蒸汽养护，严禁电热法施工。矾土水泥水化热大，放热迅速，适于浇筑很薄的构件和寒冷地区施工。在低温和干燥环境下，低水灰比矾土水泥有很强的抗硫酸盐腐蚀的能力。矾土水泥耐火性好，使用不同的耐火骨料时，可用于900～1000℃和1300～1500℃甚至1400～1600℃温度下的耐火混凝土。矾土水泥不得与硅酸盐水泥及其他能析出Ca(OH)2的胶凝材料和含CaO的物质混合使用，否则将引起迅速凝结和强度急剧下降。见高铝水泥
说明：补充资料仅用于学习参考，请勿用于其它任何用途。