1) Alumina-carbon pelletization
Al2O3-C造粒
2) Al2O3-C slide plate
Al2O3-C滑板
1.
Al-Si metal bonded Al2O3-C slide plate materials newly developed and characterized by low carbon content and low firing temperature,exhibit higher hot strength,better thermal shock resistance and better oxidation resistance than conventional Al2O3-C and Al2O3-ZrO2-C plates which are fired at much higher temperature.
自主研制开发了节能型低碳金属Al-Si结合Al2O3-C滑板,其工艺特点是低温烧成,产品特性是低碳,与常用的Al2O3-C和Al2O3-ZrO2-C滑板相比,具有较高的热态强度,较好的抗热震性和抗氧化性。
2.
The Al/Si metal bonded Al2O3-C slide plate after used are analysed by XRD, SEM, EDS and chemical analysis.
用XRD、SEM、EDS和化学分析法对金属Al/Si结合Al2O3-C滑板用后的残砖进行了分析,用后滑板的结构可分为原砖带和工作带两部分。
3) Alumina-zirconia-carbon
Al2O3-ZrO2-C
4) Al 2 O 3-SiC-C
Al2O3-SiC-C
5) Al 2 O 3-MgO-C
Al2O3-MgO-C砖
6) Al2O3-SiC-C brick
Al2O3-SiC-C砖
1.
It's proposed that,the Al2O3-SiC-C brick adhibits the molted slag due to the carbon oxidation and the big pores in the brick,while the andalusite-Al2O3-SiC brick does not adhibit the molten slag because it is free of carbon oxidation and big pores.
以大型混铁车用Al2O3-SiC-C砖和红柱石-氧化铝-SiC砖为对象,研究使用后材料粘渣的过程和原因,提出Al2O3-SiC-C质罐衬砖由于C的氧化和砖本身的气孔较大,使材料容易粘渣。
补充资料：Al
元素符号： al 英文名： aluminum 中文名： 铝
相对原子质量： 26.9815 常见化合价： +3 电负性： 1.61
外围电子排布： 3s2 3p1 核外电子排布： 2,8,3
同位素及放射线： al-26[730000y] *al-27 al-28[2.3m]
电子亲合和能： 48 kj·mol-1
第一电离能： 577.6 kj·mol-1 第二电离能： 1817 kj·mol-1 第三电离能： 2745 kj·mol-1
单质密度： 2.702 g/cm3 单质熔点： 660.37 ℃ 单质沸点： 2467 ℃
原子半径： 1.82 埃 离子半径： 0.51(+3) 埃 共价半径： 1.18 埃
常见化合物： al2o3 alcl3 al2s3 naalo2 al2(so4)3 al(oh)3
发现人： 厄斯泰德、维勒 时间： 1825 地点： 丹麦
名称由来：
拉丁文：alumen， aluminis（铝）。
元素描述：
柔软轻质的银白色金属，在地壳中含量第三。
元素来源：
自然界完全没有铝单质存在。可以电解铝土(al2o3)制取铝。
元素用途：
上自飞机下到易拉罐应用广泛。因为纯铝太柔软，所以要加入不到1%的硅或铁以加大其硬度和强度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条