1) specimen current heating dynamic hot press sintering
电流直加热动态热压烧结
1.
10%SiCp/Fe composites were fabricated by means of specimen current heating dynamic hot press sintering with iron powder with different sizes.
使用不同粒度的铁粉,采用电流直加热动态热压烧结工艺制备了10%(体积分数)的SiC颗粒增强铁基复合材料,研究了铁粉与SiC粒子颗粒级配对复合材料显微组织和力学性能的影响。
2) dynamic hot press sintering
动态热压烧结
3) heat-pressure agglomerator
加热加压烧结机
4) specimen current heating
电流直加热
1.
Manufacture of SiC particulate reinforced iron matrix composites by specimen current heating hot press sintering;
电流直加热动态热压烧结制备SiC_p/Fe复合材料
5) DC heating
直流电流加热
6) hot-press sintering
热压烧结
1.
Research on hot-press sintering process of N type thermoelectric materials ZnO;
N型热电材料ZnO热压烧结工艺研究
2.
Si_3N_4 ceramics were prepared by aligning theα-Si_3N_4 whisker in the substrate via tape casting and hot-press sintering.
利用流延成型使α-Si_3N_4晶须在基体中定向排列,并采用热压烧结技术制备了Si_3N_4陶瓷。
3.
Ti_3Al/TiC+ZrO_2 composites were prepared by mechanical alloying and hot-press sintering.
采用机械合金化和热压烧结制备了Ti3Al/TiC+ZrO2复合材料。
补充资料：活化热压烧结
分子式：
CAS号：
性质：又称反应热压烧结(reactived hot pressing sintering)或分解热压烧结(detomposition hot pressing sintering)。利用高温下粉料可能发生某种固相物理化学反应时处于较高能量的活化状态下进行热压烧结的方法。有以下几种类型：(1)相变热压烧结，如利用氧化锆在980～1100℃之间发生相变，同时进行热压，可获得高密度的细晶陶瓷；(2)分解热压烧结，如利用镁或铝的氢氧化物(或其硫酸盐)在高温下(900～1200℃)发生脱水或释气分解时，进行热压，只需加0.3～1MPa压力，保持0.5h，就可获得高密度的制品；(3)分解合成热压烧结，利用分解反应期的高度活性，在压力作用下与异类物质产生反应，然后再在压力作用下烧结成致密陶瓷，如氢氧化钡或碳酸钡分解的氧化钡与二氧化钛合成为钛酸钡等。
CAS号：
性质：又称反应热压烧结(reactived hot pressing sintering)或分解热压烧结(detomposition hot pressing sintering)。利用高温下粉料可能发生某种固相物理化学反应时处于较高能量的活化状态下进行热压烧结的方法。有以下几种类型：(1)相变热压烧结，如利用氧化锆在980～1100℃之间发生相变，同时进行热压，可获得高密度的细晶陶瓷；(2)分解热压烧结，如利用镁或铝的氢氧化物(或其硫酸盐)在高温下(900～1200℃)发生脱水或释气分解时，进行热压，只需加0.3～1MPa压力，保持0.5h，就可获得高密度的制品；(3)分解合成热压烧结，利用分解反应期的高度活性，在压力作用下与异类物质产生反应，然后再在压力作用下烧结成致密陶瓷，如氢氧化钡或碳酸钡分解的氧化钡与二氧化钛合成为钛酸钡等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条