1) morphology of eutectic carbides
共晶碳化物形态
1.
Aimed at the eutectic carbides distributed at network shape in the cast iron,the effect of heat treatment on morphology of eutectic carbides in low alloy wear resistant cast iron after deformation was studied.
针对低合金耐磨铸铁组织中共晶碳化物呈连续网状分布问题,探讨了热处理对变形低合金耐磨铸铁中共晶碳化物形态的影响。
2) eutectic carbide
共晶碳化物
1.
These structures make the quenching temperature to be rise and the overtemperature structure and the uniformity of eutectic carbide in the steel are the major reasons of quenching crack.
结果表明,由于刨齿轮W18Cr4V钢共晶碳化物不均匀度严重超标,网状碳化物、莱氏体的存在使得淬火加热温度过高,造成组织过热,增加了材料的脆性,降低了刨齿刀的力学性能,导致刨齿刀淬火时产生裂纹。
2.
Results show that, when suitable RE is added into high carbon high speed steel,the austenite and eutectic carbides have been changed.
热处理后,共晶碳化物大部分变成团球状且分布均匀。
3.
After heat treatment, network eutectic carbides of cast Cr12 die steel are changed into nodular and dispersed ones in the matrix.
铸造Cr12模具钢中共晶碳化物呈网状分布于晶界上,且枝晶粗大,经Al-Zn变质处理,共晶组织明显细化,离异共晶数量增多;经热处理后,Cr12模具钢共晶碳化物由网状变为粒状和块状且均匀分布于基体中,同时,硬度有所降低,冲击韧性得到明显提高。
3) Eutectic carbides
共晶碳化物
1.
Study of fractal dimension on the unevenness of eutectic carbides of Cr12 steel;
Cr12钢共晶碳化物不均匀度的分维研究
2.
The results show that, the morphology and distribution of the eutectic carbides are improved and the grain refinement is better with the increase of compound modifier addition within 1.
0%范围内,随着复合变质剂含量的逐渐增加,共晶碳化物的形貌和分布得到了改善,晶粒得到细化,分布趋于均匀,轧辊用高速钢的硬度略有下降,但韧性有很大提高。
3.
The result shows that the morphology and distribution of eutectic carbides in Cr12 steel under new process were improved, spheroidal pearlite and fine grain of alloy carbides were obtained,mechanics properties were enhanced.
试验结果表明,经该工艺处理的Cr12钢,组织中共晶碳化物形态和分布得以明显改善,最终热处理后获得了均匀的细隐晶回火马氏体和弥散分布的细粒状合金碳化物的显微组织,获得了优异的综合力学性能,使热处理后的拉丝模和冷冲模的使用寿命比常规热处理工艺处理的使用寿命提高1～2倍。
4) eutectic carbide granulation
共晶碳化物粒化
5) carbide morphology
碳化物形态
1.
The results show that carbide morphology had obvious effect on the wear resistance.
结果表明，碳化物形态（大小、形貌、分布及数量）对莱氏体钢的耐磨性有明显影响。
2.
The influences of heating temperature on the carbide morphology of bainite in GCr15 steel are studied.
研究了加热温度对ＧＣｒ１５ 钢贝氏体中碳化物形态的影响，结果表明，加热温度越高，上贝氏体的碳化物的长条越短； 下贝氏体中的碳化物越呈点状分布，且点状更加粗化。
6) eutectic carbide band
带状共晶碳化物
补充资料：共晶
共晶
eutectic
共晶eutectic一定成分的合金液体冷却时，转变为两种或更多紧密混合的固体的恒温可逆反应。这种反应形成的组织即为共晶组织。最简单的共晶反应是在二元合金系统中，具有共晶成分的液体L，在共晶温度下同时凝固形成两固体相a和刀共晶组织。通常用公式L禅a+刀表示。在此共晶反应温度下，出现L、a及刀三相共存。以此方式凝固的合金为共晶合金。偏离共晶成分的合金组织为亚共晶或过共晶。在冷却过程中，这些合金首先从液体中析出树枝状的先共晶组织，然后在枝晶间的液体凝固成共晶组织。可通过高的冷却速度或在液固界面高的温度梯度来抑制先共晶组织的形成，使液体可以直接通过共晶方式凝固;并可调节a及刀相的体积分量与液体的成分相适应。通常这种共晶组织又称为伪共晶。 共晶合金由于熔点低，熔化工艺相对比较简单，并且成本亦低。由于凝固的温度范围很小，改善了铸造流动性，并可抑制热缩孔、疏松及成分偏析。共晶合金具有细而分隔的多相显微组织，可以认为是具有各种特殊性能的复合材料。根据此原理，已开发出镍基和钻基共晶合金，用作抗蟠变材料，可制作喷气发动机叶片。 (汪复兴)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条