1) hypereutectic carbide
过共晶碳化物
2) eutectic carbide
共晶碳化物
1.
These structures make the quenching temperature to be rise and the overtemperature structure and the uniformity of eutectic carbide in the steel are the major reasons of quenching crack.
结果表明,由于刨齿轮W18Cr4V钢共晶碳化物不均匀度严重超标,网状碳化物、莱氏体的存在使得淬火加热温度过高,造成组织过热,增加了材料的脆性,降低了刨齿刀的力学性能,导致刨齿刀淬火时产生裂纹。
2.
Results show that, when suitable RE is added into high carbon high speed steel,the austenite and eutectic carbides have been changed.
热处理后,共晶碳化物大部分变成团球状且分布均匀。
3.
After heat treatment, network eutectic carbides of cast Cr12 die steel are changed into nodular and dispersed ones in the matrix.
铸造Cr12模具钢中共晶碳化物呈网状分布于晶界上,且枝晶粗大,经Al-Zn变质处理,共晶组织明显细化,离异共晶数量增多;经热处理后,Cr12模具钢共晶碳化物由网状变为粒状和块状且均匀分布于基体中,同时,硬度有所降低,冲击韧性得到明显提高。
3) Eutectic carbides
共晶碳化物
1.
Study of fractal dimension on the unevenness of eutectic carbides of Cr12 steel;
Cr12钢共晶碳化物不均匀度的分维研究
2.
The results show that, the morphology and distribution of the eutectic carbides are improved and the grain refinement is better with the increase of compound modifier addition within 1.
0%范围内,随着复合变质剂含量的逐渐增加,共晶碳化物的形貌和分布得到了改善,晶粒得到细化,分布趋于均匀,轧辊用高速钢的硬度略有下降,但韧性有很大提高。
3.
The result shows that the morphology and distribution of eutectic carbides in Cr12 steel under new process were improved, spheroidal pearlite and fine grain of alloy carbides were obtained,mechanics properties were enhanced.
试验结果表明,经该工艺处理的Cr12钢,组织中共晶碳化物形态和分布得以明显改善,最终热处理后获得了均匀的细隐晶回火马氏体和弥散分布的细粒状合金碳化物的显微组织,获得了优异的综合力学性能,使热处理后的拉丝模和冷冲模的使用寿命比常规热处理工艺处理的使用寿命提高1～2倍。
4) eutectic carbide granulation
共晶碳化物粒化
5) eutectic carbide band
带状共晶碳化物
6) M2C eutectic carbide
M2C共晶碳化物
1.
The cast ingots prepared using sand mould and metal mould were analyzed to investigate the effect of cooling rates on morphologies and characters of M2C eutectic carbides in M2 high speed steel.
采用砂型和金属型铸造制备M2高速钢铸锭,研究了冷却速度变化对高速钢M2C共晶碳化物形态及性质的影响,探讨了M2C共晶碳化物形态变化的机理。
2.
The effect of Al on as-cast microstructure,morphology and property of M2C eutectic carbides in M2 high speed steel was investigated,and the mechanism of morphology evolution was discussed as well.
研究Al对M2高速钢铸态组织,特别是M2C共晶碳化物形态及性质的影响,并对其形态变化机理进行了探讨。
补充资料：碳化硅晶须补强碳化硅陶瓷基复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条