1) Origin crack
裂纹源头
2) crack source
裂纹源
1.
The microstructure has been analyzed to the armor steel with attacks,it was discovered that the destruction of armored steel under the impact load is first produces the crack source in the crystal boundary intersection point,then connects mutually.
通过对冲击破坏装甲钢组织分析,发现纯净装甲钢在冲击载荷下破坏过程中是在晶界交汇处(三叉点)产生裂纹源,然后相互连接的结果。
3) crack origin
裂纹源
1.
The mechanical condition and microcharacteristics of the cleavagecrack origin of a HSLA steel are studied based on the finiteelement method(FEM)and microfractography by a scanningelectron microscope(SEM).
根据有限元计算和扫描电镜微观断口分析,本文研究了一种低合全高强度钢解理裂纹源位置的力学条件与微观特征。
4) crack initiation
裂纹发源
5) part-through crack
半露头裂纹
1.
A Line-spring model for an elliptic part-through crack in an infinite plate is established.
建立了无限平板椭圆形半露头裂纹线弹簧模型，由积分变换方法推导了问题的控制方程和应力强度因子表达式，给出了相应于表面裂纹及内埋裂纹的计算结果，通过与现有有限元解或交替迭代解比较，表明了解的良好性。
6) fatigue crack source
疲劳裂纹源
1.
Ti-60 high-temperature titanium alloy was used to determine the location of fatigue crack source by second electron image(SEI) and back electron image(BEI) technique in scanning electron microscopy.
对Ti60高温钛合金的疲劳断口进行了扫描电镜(SEM)、二次电子像(SEI)背散射电子像(BEI)分析,根据疲劳裂纹源所在位置的不同研究了Ti60高温钛合金的疲劳裂纹源位置。
补充资料：裂纹
分子式：
CAS号：
性质：材料在应力或环境(或两者同时)作用下产生的裂隙。分微观裂纹和宏观裂纹。裂纹形成的过程称为裂纹形核。已经形成的微观裂纹和宏观裂纹在应力或环境(或两者同时)作用下，不断长大的过程，称为裂纹扩展或裂纹增长。裂纹扩展到一定程度，即造成材料的断裂。裂纹可分为：交变载荷下的疲劳裂纹；应力和温度联合作用下的蠕变裂纹；惰性介质中加载过程产生的裂纹；应力和化学介质联合作用下的应力腐蚀裂纹；氢进入后引起的氢致裂纹。每一类裂纹的形成过程及机理都不尽相同。裂纹的出现和扩展，使材料的机械性能明显变差。抗裂纹性是材料抵抗裂纹产生及扩展的能力，是材料的重要性能指标之一。
CAS号：
性质：材料在应力或环境(或两者同时)作用下产生的裂隙。分微观裂纹和宏观裂纹。裂纹形成的过程称为裂纹形核。已经形成的微观裂纹和宏观裂纹在应力或环境(或两者同时)作用下，不断长大的过程，称为裂纹扩展或裂纹增长。裂纹扩展到一定程度，即造成材料的断裂。裂纹可分为：交变载荷下的疲劳裂纹；应力和温度联合作用下的蠕变裂纹；惰性介质中加载过程产生的裂纹；应力和化学介质联合作用下的应力腐蚀裂纹；氢进入后引起的氢致裂纹。每一类裂纹的形成过程及机理都不尽相同。裂纹的出现和扩展，使材料的机械性能明显变差。抗裂纹性是材料抵抗裂纹产生及扩展的能力，是材料的重要性能指标之一。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。