1) double glow plasma alloying
双层辉光离子合金化
2) Double glow plasma surface alloying technique
双层辉光离子渗金属
1.
Co-diffusion of W-Mo-Co was conducted on the surface of T8 steel by means of the double glow plasma surface alloying technique.
采用双层辉光离子渗金属技术在T8钢表面进行了W-Mo-Co多元共渗,研究了表面合金层的组织、相组成、成分、硬度、脆性以及与基体的结合强度。
3) double glow plasma surface alloying
双层辉光离子渗金属
1.
By using the character of high temperature and high energy of plasma,stainless steel,high speed steel,nickel base alloy and superalloy are obtained on metal surface by double glow plasma surface alloying.
双层辉光离子渗金属技术利用等离子体温度和能量密度高的特点,在金属材料表面形成不锈钢、高速钢、镍基合金和超合金,改善金属零件表面的耐磨性能,提高其使用寿命,开创了表面冶金的新领域。
2.
Diffusion and deposition compound layers of Fe-W-Mo-Co were formed on the surface of ingot iron and 20 steel by means of the double glow plasma surface alloying technique.
采用双层辉光离子渗金属技术,在工业纯铁和20钢表面进行W、Mo、Co多元共渗,形成Fe W Mo Co型渗镀复合层。
3.
A TiN coating is in-situ synthesized on TC11 alloy surface by double glow plasma surface alloying technique to improve its wear resistance.
采用双层辉光离子渗金属技术在钛合金TC11表面原位合成TiN渗镀层以提高其耐磨性。
4) double glow discharge alloying process
双层辉光等离子渗金属
5) double glow discharge technique
双层辉光离子渗金属
1.
Molybdenum surface alloying layer was prepared on Ti6Al4V substrate using double glow discharge technique.
利用双层辉光离子渗金属技术在Ti6Al4V合金表面渗Mo,用球-盘磨损试验机对试样的摩擦性能进行了研究。
2.
Surface alloying layer of molybdenum on Ti6Al4V base was formed by double glow discharge technique.
利用双层辉光离子渗金属技术在Ti6Al4V表面渗Mo,形成了表面改性合金层,就910～990℃渗Mo时基体温度对表面合金层性能的影响进行了研究。
6) double glow plasma surface alloying
双辉等离子表面合金化
补充资料：双[1-(4-二甲氨基)苯基2-苯基1,2-二硫代乙烯合镍]
分子式：
CAS号：
性质：紫黑色单斜晶体。熔点277～278℃。溶于苯、甲苯、三氯甲烷等大多数有机溶剂。红外频率υ(C＝S)1190、1165、1140cm-1,红外频率υ(S-C-C-S)880cm-1。由对二甲氨基安息香、五硫化二磷在二噁烷(二氧六环)中反应后,加入镍(Ⅱ)盐溶液制得。用作光学非线性材料。
CAS号：
性质：紫黑色单斜晶体。熔点277～278℃。溶于苯、甲苯、三氯甲烷等大多数有机溶剂。红外频率υ(C＝S)1190、1165、1140cm-1,红外频率υ(S-C-C-S)880cm-1。由对二甲氨基安息香、五硫化二磷在二噁烷(二氧六环)中反应后,加入镍(Ⅱ)盐溶液制得。用作光学非线性材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条