1) Sulphoaluminate cement concrete
硫铝酸盐水泥混凝土
2) Ba-containing sulphoaluminate cement concrete
含钡硫铝酸盐水泥混凝土
3) Aluminate cement concrete
铝酸盐水泥混凝土
4) Portland cement refractory concrete
硅酸盐水泥耐火混凝土
5) portland cement concrete
硅酸盐水泥混凝土
1.
In this thesis, a comparative experimental investigation was conducted to study explosive spalling and residual mechanical properties of Portland cement concrete, sulphoaluminate cement concrete and high aluminate cement concrete at the same strength level at room temperature.
本文进行了同强度的硅酸盐水泥混凝土、铝酸盐水泥混凝土与硫铝酸盐水泥混凝土的高温爆裂性能和高温后残余力学性能的对比性试验研究。
6) sulphoaluminate cement
硫铝酸盐水泥
1.
A systematic study of autogenously pulverizable sulphoaluminate cement,Part one:Preparation and properties;
自粉化硫铝酸盐水泥系列研究之一——自粉化水泥制备及其性能研究
2.
Research of durability of sulphoaluminate cement based concrete with mineral admixture;
掺合料对硫铝酸盐水泥基混凝土耐久性影响的研究
3.
Influence of several kinds of admixtures on the properties of sulphoaluminate cement;
几种外加剂对硫铝酸盐水泥性能的影响
补充资料：硫铝酸盐水泥
分子式：
CAS号：
性质：用低品位的矾土和石膏、石灰按适当比例混合磨细后，在1300℃±50℃的回转窑中制得以无水硫铝酸钙(3CaO3Al2O3·CaSO4)和β-2CaO·SiO，占18％～30％为主要矿物的熟料，按与硫铝酸盐的不同摩尔比M加入石膏，可得不同性质的硫铝酸盐水泥。当M=0～1时，为快硬早强水泥，可用于抢修工程；当M=1～2时，可制得微膨胀水泥，用于锚固和刚性防水工程；M>2时，可制成自应力水泥，用于制管工程。
CAS号：
性质：用低品位的矾土和石膏、石灰按适当比例混合磨细后，在1300℃±50℃的回转窑中制得以无水硫铝酸钙(3CaO3Al2O3·CaSO4)和β-2CaO·SiO，占18％～30％为主要矿物的熟料，按与硫铝酸盐的不同摩尔比M加入石膏，可得不同性质的硫铝酸盐水泥。当M=0～1时，为快硬早强水泥，可用于抢修工程；当M=1～2时，可制得微膨胀水泥，用于锚固和刚性防水工程；M>2时，可制成自应力水泥，用于制管工程。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。