1) Hstainless steel mesh substrate
不锈钢丝网基底
2) stainless steel wire mesh
不锈钢丝网
1.
The effect of preparation parameters on the structure and catalytic performance of Ce-Pt-Pd/SSWM stainless steel wire mesh catalyst
制备参数对不锈钢丝网催化剂结构和性能的影响
3) stainless wire mesh
不锈钢网丝
1.
Analysis present that pitting corrosion and stress corrosion are the mainly reasons for the crack of stainless wire mesh.
结果表明,不锈钢网丝的点腐蚀和应力腐蚀是造成网丝断裂的根本原因,由于不锈钢网丝的断裂,导致波纹管失去丝网的保护和轴向伸长的约束,波纹管在内压作用下冲破丝网的约束,进而产生过度弯曲变形,在波纹管与短接管焊接的薄弱处因过载而发生断裂。
4) stainless steel substrate
不锈钢基底
1.
The (002) directional Yttria Stabilized Zirconia (YSZ) buffered layer film was deposited on the stainless steel substrate with the Ar + ion beam assistence at room temperature,and then the YBa 2Cu 3O 7-x (YBCO) film was deposited on the YSZ/stainless steel substrate at 750℃ by pulsed laser ablation.
室温下应用Ａｒ＋ 离子源辅助准分子脉冲激光沉积（００２）取向的ＹＳＺ（Ｙｔｔｒｉａ－ｓｔａｂｉｌｉｚｅｄ ｚｉｒｃｏ－ｎｉａ）过渡层薄膜于不锈钢基底上；基底加温至７５０℃，用准分子脉冲激光沉积高电流密度ＹＢＣＯ（ＹＢａ２Ｃｕ３Ｏ７－ ｘ） 高温超导线材。
2.
CeO2 films were deposited by pulsed laser ablation on stainless steel substrates at room temperature with the Ar+ ion beam assistance.
室温下在不锈钢基底上应用Ar+离子源辅助，准分子脉冲激光沉积了CeO2薄膜。
3.
The (002) directional Yttria-Stabilized Zirconia (YSZ) buffered layer film was deposited on the stainless steel substrate with the Ar~+ ion beam asslstence at room temperature,and then the YBa_2Cu_3O_(7-x) (YBCO) film was deposited on the YSZ/stainless steel substrate at 750℃ by pulsed laser ablation.
室温下应用Ar~+离子源辅助准分子脉冲邀光沉积(002)取向的YSZ(Yttria-stabilized zirconia)过渡层薄膜于不锈钢基底上;基底加温至750℃,用准分子脉冲激光沉积高电流密度YBCO(YBa_2Cu_3O_(7-x))高温超导线材。
5) stainless steel wire
不锈钢丝
1.
Technology of removing deformation magnetic property of metastable austenite stainless steel wire
消除亚稳定奥氏体不锈钢丝形变磁性的技术
2.
The microstructure and mechanical properties of stainless steel wires used for metal rubber were studied by means of optical microscopy,SEM,and X-ray diffraction.
15mm的Cr-N i-Mn系不锈钢丝的微组织结构和力学性能的变化规律。
3.
There is a coat of oxide on the surface of the heat treated stainless steel wire,which is difficult to be cleaned.
不锈钢丝热处理后表面形成一层难以清除的氧化皮 ,4 80℃高温碱煮和 85℃高锰酸钾碱液的清洗对比试验和应用显示高锰酸钾碱洗工艺可行 ,但要求KMnO4 和NaOH浓度大于 80g L ,溶液温度高于 80℃ ,清洗时间5～ 10min ,比碱煮少 5min ;高锰酸钾碱液清洗效果好 ,不锈钢丝表面无黑色胶状物 ,而且不会产生过腐蚀 ,每吨不锈钢丝可节省电能 1875kW·h ,劳动环境也有很大改
6) stainless steel mesh
不锈钢网
1.
The LaNiO3 film was synthesized on the stainless steel mesh(SSM).
在不锈钢网(SSM)表面上合成了LaNiO3催化剂前驱体薄膜。
补充资料：钢丝网
钢丝网
steel wire mesh
gongSIW0ng钢丝网(steel wire mesh)由钢丝编织或焊接而成的具有网孔的钢丝制品。钢丝网广泛应用于冶金、矿山、国防及工农业生产等各个部门，做筛选、防护、隔离、建筑材料之用。 分类和规格丝网根据使用场所和使用性能的不同有几十个品种。按有无镀层分，有光面钢丝网、镀锌钢丝网、涂塑钢丝网;按材料性质分，有普通低碳钢丝网、耐热合金钢丝网、耐蚀不锈钢丝网;按加工方式分，有编织钢丝网和焊接钢丝网。钢丝网的规格型号以钢丝、网孔和网幅表示。网丝用线号或英寸、毫米表示，网孔用孔径、网目或网号表示。网目指1英寸长度内网孔的个数，英美等国常以网目表示网孔大小，中国以孔径或网目表示之，前苏联以网号表示。网号指网孔的公称尺寸，如1.0号网指正方形孔每边长1.omm。 品种及工艺常见的钢丝网品种及网孔形状如图所示，有方形孔、菱形孔、六角孔、梯形孔等数种。方形孔有波形方孔(眼)网、镀锌电焊网、平纹网几种。波形方孔网又称拨花网或轧花网，如图a所示，网的经线和纬线经过预先弯曲成波状，再行织造，网孔结合牢固，网孔方正，抗拉力好，耐磨性强，不易变形。镀锌电焊方孔网，如图b所示，结构坚固，整体性强，点焊后再电镀，具有很好的防蚀能力。菱形网亦称斜方孔网，如图‘所示，一般用低碳镀锌钢丝预先扭成扣状，然后编织。使用时网边须拉紧，否则网扣易松弛，影响网的整体性。六角网亦称拧花网、龟甲网，如图d所示。网孔为六角形，按加工工艺有先镀后编织和先编织后镀两种。图h所示是一种带加强筋的六角网，抗拉力比一般六角网大，布筋间隔根据用途而有所不同。梯形网如图e所示，网孔呈梯形，主要用于建材中作波瓦和保温墙的加强网。另一种矿筛网如图f所示，用于筛选矿石，网孔较粗，丝径为5.omm或6.otnm，单位网面工作压力达1一1.skPa。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条