1) H stainless steel wire
304H不锈钢丝
2) 304H S.S
304H不锈钢
3) stainless steel wire
不锈钢丝
1.
Technology of removing deformation magnetic property of metastable austenite stainless steel wire
消除亚稳定奥氏体不锈钢丝形变磁性的技术
2.
The microstructure and mechanical properties of stainless steel wires used for metal rubber were studied by means of optical microscopy,SEM,and X-ray diffraction.
15mm的Cr-N i-Mn系不锈钢丝的微组织结构和力学性能的变化规律。
3.
There is a coat of oxide on the surface of the heat treated stainless steel wire,which is difficult to be cleaned.
不锈钢丝热处理后表面形成一层难以清除的氧化皮 ,4 80℃高温碱煮和 85℃高锰酸钾碱液的清洗对比试验和应用显示高锰酸钾碱洗工艺可行 ,但要求KMnO4 和NaOH浓度大于 80g L ,溶液温度高于 80℃ ,清洗时间5～ 10min ,比碱煮少 5min ;高锰酸钾碱液清洗效果好 ,不锈钢丝表面无黑色胶状物 ,而且不会产生过腐蚀 ,每吨不锈钢丝可节省电能 1875kW·h ,劳动环境也有很大改
4) stainless steel flat wire
不锈钢扁丝
5) stainless steel filament
不锈钢长丝
1.
The composite yarn of acrylic & stainless steel filament wrapped yarn was spun by wrapped machine,and was used for anti-electrostatic knitted material.
利用包覆纺丝机,以包缠纺复合成纱工艺研制开发了腈纶/不锈钢长丝包缠纱,并用之织作防静电针织面料。
6) stainless steel pole thread
不锈钢极丝
补充资料：不锈钢
| 不锈钢 stainless steel 耐空气、蒸汽、水等弱腐蚀介质和酸、碱、盐等化学浸蚀性介质腐蚀的钢。又称不锈耐酸钢。实际应用中，常将耐弱腐蚀介质腐蚀的钢称为不锈钢，而将耐化学介质腐蚀的钢称为耐酸钢。由于两者在化学成分上的差异，前者不一定耐化学介质腐蚀，而后者则一般均具有不锈性。不锈钢的耐蚀性取决于钢中所含的合金元素。铬是使不锈钢获得耐蚀性的基本元素，当钢中含铬量达到12％左右时，铬与腐蚀介质中的氧作用，在钢表面形成一层很薄的氧化膜（ 自钝化膜），可阻止钢的基体进一步腐蚀。除铬外，常用的合金元素还有镍、钼、钛、铌、铜、氮等，以满足各种用途对不锈钢组织和性能的要求。不锈钢通常按基体组织分为：①铁素体不锈钢。含铬12％～30％。其耐蚀性、韧性和可焊性随含铬量的增加而提高 ， 耐氯化物应力腐蚀性能优于其他种类不锈钢。②奥氏体不锈钢。含铬大于18％，还含有 8％左右的镍及少量钼、钛、氮等元素。综合性能好，可耐多种介质腐蚀。③奥氏体 - 铁素体双相不锈钢。兼有奥氏体和铁素体不锈钢的优点，并具有超塑性。④马氏体不锈钢。强度高，但塑性和可焊性较差。
|
说明：补充资料仅用于学习参考，请勿用于其它任何用途。