1) preimmerse with magnesium alloy
预加镁合金浸泡
2) Foam Magnesium Alloy
泡沫镁合金
1.
Safe Problems in Manufacturing of Foam Magnesium Alloy by Vacuum Infiltration;
真空渗流法制备泡沫镁合金的工艺安全问题
2.
The preparation process of foam magnesium alloy by vacuum infiltration,which includes the choice of filling,fabrication of prefabricated block and vacuum infiltration,was studied.
研究了真空渗流法制备泡沫镁合金的工艺,具体包括填料的选择,预制块的制作和真空渗流三个部分。
3) AZ91 magnesium alloy foam
AZ91镁合金泡沫
1.
The AZ91 magnesium alloy foam with a diameter of 9mm was fabricated by using vacuum melt infiltration and water quenching methods.
压缩试验结果表明,AZ91镁合金泡沫材料的塑性变形能力明显高于铸态AZ91镁合金。
4) Al-Mg alloy foam
泡沫铝镁合金
1.
Investigation on compressive behavior and energy absorbing property of Al-Mg alloy foams;
泡沫铝镁合金的压缩与吸能性的研究
5) pre-soaking
预浸泡
1.
This article texts the detoxify of phytic acid to Cadmium garlic by adding directly and pre-soaking in water.
本实验用植酸以直接加入和预浸泡两种方式3种方法处理镉蒜,通过测量处理前后的蒜根平均长度,测定根、茎、叶中的镉含量及不同部位镉的不同存在形式的含量,分析比较出采用植酸对镉蒜的最佳解毒方式。
6) Processing technique of magnesium alloys
镁合金加工技术
补充资料：镁铝锌系铸造镁合金
镁铝锌系铸造镁合金
magnesium-aluminium-zinc cast magnesium alloy series
mellUxlnx一zhuzao melhej一n镁铝锌系铸造镁合金(magnesium一alumini-um一Zine east magnesium alloy series)以铝、锌为主要合金化元素的铸造镁合金，可用于砂型和金属型铸造，也可用于压力铸造，具有良好的流动性和焊接性能，热裂倾向性低，但有较大的显微疏松倾向。 中国牌号ZM一5(7.5%一9.0%Al，0.15%一0.5%Mn，0.2%一0.8%Zn，Mg为余量)合金，ZM一10(9 .0%~1 0.2%AI，0.15%一0.5%Mn，0.2%一0.8%zn，Mg余量)合金。zM一5合金为镁铝锌系铸造镁合金的代表，相当于前苏联牌号的M月5合金。合金中杂质为铁、铜、镍、硅、钻等，根据需要可适量加些被。 铝是主要合金化元素并含有锌和锰，通过改变铝、锌含量可改变合金的力学性能、铸造性能及抗蚀性能。铝含量的增加能进一步改善合金的铸造性能和提高合金的强度，但使伸长率和抗腐蚀性能降低。加入少量的锌和锰能显著提高合金的抗蚀性能，还可以提高合金的强度。但锌含量增加会使合金的缩松倾向增加。ZM一5合金的铸态组织由固溶体叔Mg)为基体，沿它的晶界以不连续网状分布着y(Mg‘A13)相，以及分布在固溶体叔Mg)中的Mn一Ai化合物小质点所组成。热处理强化常采用两种规范:(1)淬火(T4):加热到370~380℃保温2一4h，再升温至415士5℃保温12一16h，然后在空气中冷却。(2)淬火时效(T6):淬火后再在175士5℃人工时效16h。ZM一5合金的力学性能见表1。 表1 zM一5合金的力学性能详 镁铝锌系铸造镁合金结晶间隔较大，充型能力良好，铸造工艺性能及物理常数见表2。表2 zM一s合金铸造工艺性能及物理常数}牛粉粉{字朴 镁铝锌系铸造镁合金能铸出外形和内腔形状复杂的铸件，加之镁合金在汽油、煤油、润滑油中很稳定，因而多用于航空工业的燃油系统和润滑系统。还可作为在受冲击载荷时能吸收大量能量的零部件及飞机着陆轮的轮毅。 (杨朴)