1) yield-point phenomena
屈服点现象
1.
As a first approach, a viscoplastic constitutive model based on the assumption of rapid dislocation multiplication is proposed to describe such high temperature yield-point phenomena.
钛合金由于常温具有强烈的回弹倾向,因此常采用温间压力成形进行成形处理,但是许多钛合金在β相变点以上的应力应变曲线表现出明显的屈服点现象、急剧的屈服应力下降、应变软化以及强烈的应变速率敏感性。
3) yield phenomenon
屈服现象
1.
To introduce the mechanism of yield phenomenon occurring in the process of metal material tensile test.
介绍金属材料在拉伸试验过程中出现屈服现象的机制,指出上、下屈服点出现的原因。
4) yield point
屈服点
1.
Cause analysis of unobvious yield point of low carbon steel hot-rolled wire rod
低碳钢热轧盘条屈服点不明显的原因分析
2.
The chemical components and microstructure are analyzed for the hot-rolled reinforced bar,of which the yield point is not so clear,some measures proposed.
对存在屈服点不明显问题的热轧带肋钢筋的化学成分和组织进行了分析,提出了改进措施。
3.
To analyze the cause of cold bending brittle fracture and without yield point phenomenon of 20MnSi reinforced bar.
对 2 0MnSi钢筋冷弯脆断和无屈服点现象进行原因分析 ,钢中异常组织粒状贝氏体的存在是造成冷弯脆断和无屈服点的直接原因 ,而C ,Mn含量偏高又是异常组织粒状贝氏体产生的原因。
5) yield vertex
屈服顶点
6) Secondary yield point
次屈服点
补充资料：屈服
屈服
yield
屈服yield在外加应力下，材料开始发生不可逆的范性变形的现象。连续加载过程中，应力不增加或开始有所降低而材料如能继续变形，这种材料便具有明显的屈服现象，此时材料所承受的恒定、最大或最小应力分别称为材料的屈服点(飞)、上屈服点(隽u)或下屈服点(asL)。低碳钢及其他含有少量填隙元素的体心立方金属等都具有明显的屈服点:而不锈钢、面心立方金属及密集六角结构金属则无明显的屈服点。对于没有明显屈服现象的材料，很难准确测定它们发生塑性流变的起始点，工程上一般取永久变形值达0.2%时所对应的应力值为该材料的屈服强度，以a02表示。 屈服现象与材料中位错的形成、增殖及运动有关。体心立方金属中位错受到钉扎，不易运动，而且位错的运动速率对应力不敏感，可滑移位错的形成便标志着范性形变的开始，因而具有明显的屈服点。而面心立方金属中位错的运动速率对应力非常敏感，原生位错在低应力下就能运功，使面心立方金属不存在明显的屈服点。 (李宗全)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。