1) non-yield point
无屈服点
1.
Accoding to results of the test,relevant game of controlling cold bending brittle failure and non-yield point of 20MnSi screw-thread reinforcement was proposed.
对２０ＭｎＳｉⅡ 级螺纹钢中异常金相组织粒状贝氏体的形成机理进行了实验研究和定量分析以及相应的现场试验工作， 并根据试验结果提出了控制螺纹钢筋冷弯脆断和无屈服点的相应对策。
2) no yield point
无屈服点
1.
This paper analyses and researches the cause of no yield point in tensile test and brittle fracture in cold bending test of 20MnSi HRB.
分析和研究了20MuSi热轧带肋钢筋在常规力学性能检验中偶然出现冷弯脆断和无屈服点异常现象的原因。
2.
However, no yield point of the steel pipe filled with concrete are not involved; The model tests of concrete-filled steel tubular lace.
国内外许多学者对钢管混凝土结构的力学性能和设计方法进行了大量的研究工作,但对无屈服点的钢管所组成的钢管混凝土结构(以下简称无屈服点钢管混凝土结构)却涉及很少。
3) Noyieldpoint
无屈服
1.
in the article, the 4 batches of Noyieldpoint the 400 MPa hot rolled ribbed bar are analysed, and some measures are put forward to resolve the existing problems.
对试制过程中四炉无屈服含铌 4 0 0 MPa级热轧带肋钢筋进行了分析 ,并提出解决问题的对
4) yield point
屈服点
1.
Cause analysis of unobvious yield point of low carbon steel hot-rolled wire rod
低碳钢热轧盘条屈服点不明显的原因分析
2.
The chemical components and microstructure are analyzed for the hot-rolled reinforced bar,of which the yield point is not so clear,some measures proposed.
对存在屈服点不明显问题的热轧带肋钢筋的化学成分和组织进行了分析,提出了改进措施。
3.
To analyze the cause of cold bending brittle fracture and without yield point phenomenon of 20MnSi reinforced bar.
对 2 0MnSi钢筋冷弯脆断和无屈服点现象进行原因分析 ,钢中异常组织粒状贝氏体的存在是造成冷弯脆断和无屈服点的直接原因 ,而C ,Mn含量偏高又是异常组织粒状贝氏体产生的原因。
5) yield vertex
屈服顶点
6) Secondary yield point
次屈服点
补充资料：低屈服点钢
分子式：
CAS号：
性质： 屈服点相对较低的钢。这种钢具有优良的深冲性能和深拉延性能，容易变形加工制造形状复杂的钢制品。典型的低屈服点钢如08F钢，它的屈服点只有176MPa左右，在各类钢中其屈服点显著偏低。用这种钢的薄板可制造深冲压和深拉延的制品，如各种贮器，搪瓷制品、仪表板以及管件等。
CAS号：
性质： 屈服点相对较低的钢。这种钢具有优良的深冲性能和深拉延性能，容易变形加工制造形状复杂的钢制品。典型的低屈服点钢如08F钢，它的屈服点只有176MPa左右，在各类钢中其屈服点显著偏低。用这种钢的薄板可制造深冲压和深拉延的制品，如各种贮器，搪瓷制品、仪表板以及管件等。