1) intergranular space
颗粒间空隙; 晶间间距
2) void among particles
颗粒间的空隙
3) interparticle spacing
颗粒间距
4) dendritic distance
枝晶间距
1.
The results show that the variety of segregation parameter is the highest when dendritic distance is 80 μm～120 μm,and the calculated and experimented result of segregation index δ has a .
研究结果认为:偏析指数的变化量Δδ在枝晶间距为80μm～120μm时减小量最大,并且在枝晶间距为120μm的条件下,合金在1160℃退火8h和16h的Nb元素的δ计算值与实验值较符合。
5) dendrite arm spacing
枝晶间距
1.
Quantitative relationship between secondary dendrite arm spacing and solidification cooling rate of AZ31 magnesium alloy;
AZ31镁合金的凝固冷却速率与二次枝晶间距的定量关系
2.
Secondary dendrite arm spacing(DAS) was measured by transvesal method of quantitative metallographic analysis,and the microstructure characters under different solidification cooling rates were analyzed briefly.
用定量金相分析之截线法测定了各个试样的二次枝晶间距,并对不同凝固冷却速度下的组织特征做了简要分析。
3.
The ascast microstructure, chemical composition segregation, dendrite arm spacing, gas content, inclusion and microstructure evolution during CSP rolling process were investigated.
对CSP的铸坯组织、化学成分偏析、枝晶间距、气体含量、夹杂物以及轧制过程中的组织变化进行了研究,结果表明:CSP薄板坯的低倍组织在结构上和传统板坯没有本质区别,但薄板坯组织较为细密,柱状晶比较发达,一次枝晶与二次枝晶间距小,化学成分均匀,铸坯全氧含量为28×10-6,氮含量为47×10-6;第一道次轧制后中心部的疏松和偏析明显减轻,树枝晶沿轧制方向弯曲,但没有被打碎;CSP铸坯中大颗粒夹杂物较少,主要是外来的;内生夹杂物主要以含氧化铝和铝酸盐及氧化钙的为多,尺寸基本都在10μm以内,大部分在2～5μm。
6) cellular spacing
胞晶间距
1.
4% Mn alloy on a 5?kW CW CO 2 laser were carried out to study the effects of processing parameters (scanning velocity, laser output power) on the growth direction of microstructure in the molten pool and cellular spacing selection under ultrahigh temperature gradient and rapid directional solidification conditions.
4 %Mn合金进行了一系列表面重熔实验 ,就激光束扫描速度对重熔区微观组织生长方向的影响和超高温度梯度快速定向凝固条件下胞晶间距选择规律进行了研究。
2.
3%Mn alloy to investigate the response of microstructure pattern and cellular spacing selection to the variation of growth rate.
３％Ｍｎ进行了系列表面熔凝实验，对该合金的组织形态和胞晶间距选择规律进行了研 究结果表明：随着生长速度的提高，组织形态由低速平界面向细胞晶和高速绝对稳定平界面转变在快速凝固条件下。
3.
4%Mn alloy to investigate the response of microstructure pattern and cellular spacing selection to the variation of growth rate.
利用连续波CO2 激光器对Cu 31 4 %Mn进行了系列表面熔凝实验 ,对该合金的组织形态和胞晶间距选择规律进行了研究 。
补充资料：颗粒
分子式：
CAS号：
性质：指小而圆的物质。最简单的颗粒形状是圆球。粒径在40～500μm范围内，气固密度差在1400～4000kg/m3之间的颗粒称粗颗粒(coarse particle)；粒径在20～100μm范围内，气固密度差小于1400kg/m3的颗粒称细颗粒(fime particle)；由许多个粒度间隔不大的粒级颗粒构成的颗粒系统称颗粒群(particle swarm)。
CAS号：
性质：指小而圆的物质。最简单的颗粒形状是圆球。粒径在40～500μm范围内，气固密度差在1400～4000kg/m3之间的颗粒称粗颗粒(coarse particle)；粒径在20～100μm范围内，气固密度差小于1400kg/m3的颗粒称细颗粒(fime particle)；由许多个粒度间隔不大的粒级颗粒构成的颗粒系统称颗粒群(particle swarm)。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条