1) dispersion strengthened materia
弥散强化材料
2) surface dispersion on Cu
表面弥散强化Cu基材料
3) ZGSPt"TriM"
弥散强化铂复合材料
4) dispersion-hardened material
弥散硬化材料(冶)
5) Al_2O_3 dispersion strengthened copper composite
Al2O3弥散强化铜基复合材料
1.
The fabrication processes of Al_2O_3 dispersion strengthened copper composite are reviewed in this paper.
综述了Al2O3弥散强化铜基复合材料的各种制备工艺及研究进展,对内氧化法制备Al2O3弥散强化铜基复合材料进行了详细的阐述。
6) Al_2O_3 dispersion strengthening Cu-based composite
Al_2O_3弥散强化铜基复合材料
1.
The progress of Al_2O_3 dispersion strengthening Cu-based composite prepared by internal oxidation was reviewed;the medium of internal oxidation and the conditions of thermodynamics and kinetics were summed up;the combination processes of Al_2O_3 dispersion strengthening Cu-based composite prepared by internal oxidation were described in detail.
综述了内氧化法制备Al_2O_3弥散强化铜基复合材料的研究进展,总结了Cu-Al合金内氧化介质及热力学和动力学条件,对内氧化法制备Al_2O_3弥散强化铜基复合材料进行了详细的阐述。
补充资料：弥散强化材料
弥散强化材料
disPersion strellglhened materials
弥散强化材料dispersion strellgt比ned materials用粉末冶金方法制备的，氧化物质点弥散分布在金属基体中的材料。 最早制造的弥散强化材料是韧而不下垂的钨丝。此后相继出现了烧结铝(AD、无氧铜(Cu)以及镍(Ni)和铁(Fe)基弥散强化材料。氧化物质点在基体中的分布间距一般不大于0.3召m。通常对氧化物的要求是:尺寸在1召m以下;熔点高;在基体中不溶解;相界面能低，结合牢固;生成自由能高，不容易分解。常用的氧化物有三氧化二铝(A1203)、二氧化牡(ThOZ)和三氧化二忆(Y203)等。弥散强化材料有优良的高温性能，甚至在接近基体金属熔点时，仍有足够的强度;组织稳定，再结晶温度高;有良好的导热和导电性能。 常用的弥散强化材料有:①弥散强化镍:用TllO2作为弥散强化相。又称TD一Ni。其强化相质点用0.1尽m的ThOZ粉末悬浮在镍盐溶液中共沉淀产生。TD-Ni合金有良好的高温性能，可用来制作火焰筒等高温零件。②弥散强化高温合金:由热稳定性好的超细氧化物质点作强化相，它兼有沉淀强化和弥散强化两种机制。因主要应用机械合金化(MA)工艺，故又称MAODS合金。在氧化物弥散强化(ODS)高温合崖性能较好的是用YZO3加部分A1203粒子强化的铁镍基合金。MA6000、MA754以及MA956合金于制造涡轮发动机的燃烧室、、隔热板及其他耐高部件。 弥散强化材料所用的粉末原料，通常用机械合工艺制备，即用干式高能球磨机研磨原料，得到结细、且均匀复合的粉末。原料粉包括粒度为1一20}的纯金属粉(Ni、Cr、Fe、Co、W、Mo)和氧含制在 0.2%以下的母合金粉(Ni与Al、Ti、Zr、以及难熔化合物。粉末颗粒在高能球磨时，经受剧形和反复破碎，在新暴露的表面产生“冷焊”，焊接颗粒进而又被破碎。如此反复地进行复合和破碎，出化学成分均匀、粒度细小的粉末。 将粉末原料用热挤压或热等静压成型工艺进行和固结，使其致密化。挤压温度、挤压比、流动应挤压速度是粉末挤压致密化工艺的主要参数。热等是用惰性气体(Ar)作介质，用金属包套封装粉末如使其热致密化。热致密化成型的合金组织为微细的晶，这种组织在适宜的温度和应变速率下有超塑性温加工性能优良。(姜振j电 和用零跳撇哪缈和胶狱糙型和压乳轴高迎拼摊料料.咋)