1) knife-line attach
刀切状腐蚀
2) knife line attack
刀状腐蚀
1.
The problem of the knife line attack of welded joint is soluted,the life of welding impeller made of Cr17Ni2 steel is prolonged and it gets evident economical benefit.
采用二次稳定化退火处理 ,解决了 Cr17Ni2钢异质焊接接头刀状腐蚀的问题。
3) knife-line attack
刀线腐蚀
4) knife corrosion
刀口腐蚀
5) filiform corrosion
丝状腐蚀
1.
This paper introduced evolvement,feature,mechanism,harm and prevention of filiform corrosion.
丝状腐蚀是一种线型的涂膜下腐蚀,20世纪60年代在钢质药筒的储存过程中发现,并进行了大量的研究工作。
2.
The filiform corrosion phenomenon of coated aluminum was found.
对铝合金汽车轮毂在海南万宁试验站进行为期24个月的棚下 和户外暴露试验,发现涂膜下铝合金发生丝状腐蚀。
6) corrosion status
腐蚀状况
1.
The corrosion environment, corrosion status, corrosion mechanisms and protection measures taken for the crude distillation unit processing Liaohe high-acid value crude in Jinxi Refining and Chemical Complex were introduced.
介绍了锦西炼油化工总厂蒸馏装置炼制高酸值辽河油的腐浊环境、腐蚀状况、腐蚀机理和采取的防护措施。
2.
The corrosion environment of an underground drift of one coal mine and the corrosion status of in-situ split-set bolts,which are embedded in the drift for 10 years,have been investigated.
调查了河南焦作煤矿地下巷道腐蚀环境和现场10a期管缝式锚杆腐蚀状况,对地下水腐蚀物含量、锚杆宏观质量损失和局部坑蚀情况实施了测量,并对锚杆杆体极限承载力和塑性性能进行测试。
补充资料：刀状侵蚀
分子式：
CAS号：
性质：晶间腐蚀的一种类型，主要发生于含钛或铌的奥氏体不锈钢焊接件上。腐蚀区域紧邻焊缝，窄而深，状如刀口。焊接后对工件进行1050℃固溶处理可以防止。
CAS号：
性质：晶间腐蚀的一种类型，主要发生于含钛或铌的奥氏体不锈钢焊接件上。腐蚀区域紧邻焊缝，窄而深，状如刀口。焊接后对工件进行1050℃固溶处理可以防止。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。