1) cinder pig iron
夹渣生铁
2) iron oxide slag inclusion
氧化铁夹渣
1.
The defect was analyzed by metallographic examination,the result showed that the defect was iron oxide slag inclusion.
结果表明:该缺陷是氧化铁夹渣物。
3) cinder pig iron
炉渣生铁
4) cinder pig iron
含渣生铁
5) slag
[英][slæɡ] [美][slæg]
夹渣
1.
Analysis of factors influencing slag defects in ductile iron castings;
球铁件夹渣缺陷形成的影响因素分析
2.
Solution to the slag of wedge surface sealing in brass valve;
解决铸造黄铜闸板密封面夹渣缺陷的措施
3.
The results show that local slag of the parent pipe is the main cause of the bend cracking.
结果表明,弯管母管局部存在的夹渣是造成弯管开裂的主要原因,而弯管热煨温度偏高,造成外弧侧材料产生过热,管体材料冲击韧性降低,加速了外弧侧管体裂纹失稳扩展。
6) inclusion
[英][ɪn'klu:ʒn] [美][ɪn'kluʒən]
夹渣
1.
Based analysis for mechanism of inclusion defect in eletroslag billet of H.
通过对高速钢电渣锭夹渣缺陷机理分析,采取合理设定重熔工艺参数和重熔前进行捅渣操作,减少了结晶器挂渣现象,大幅度减少了电渣锭夹渣缺陷。
2.
The results indicated that the linear defects resulted from the big inclusions such as SiO_2,CaO,Al_2O_3 and Na_2O.
针对45#钢螺栓表面线状缺陷进行了低倍、金相、电子探针等检测分析,结果表明,线状缺陷由大型夹渣造成,其主要成分为SiO2、CaO、Al2O3、Na2O,系连铸过程中酸性钢水中包覆盖剂卷入所致。
3.
A certain numbers of gas porosity and inclusion defects occur in production of X80 grade φ1 219 mm×18.
4 mm螺旋埋弧焊管生产过程中产生一定量的气孔和夹渣缺陷,分别从成型稳定性、卷板质量、焊接规范、焊剂等方面对其形成原因进行了分析,并提出了一些应对措施。
补充资料：夹渣
夹渣
slag patch
J Iazha夹渣(s lag Patch)在浇注过程中，浇注系统中的泥砂、熔蚀的流钢砖或脱氧产物，从模内钢液中浮出来，被正在凝固的锭壳捕获，而形成的钢锭缺陷，亦称夹砂。当保护渣熔化不良时，也会被上升的钢液卷入表层而形成夹渣。这种缺陷会造成轧材夹砂。其防止措施主要是改善脱氧工艺，仔细清扫浇注系统以及改善保护渣配方。 (汪建农)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。