1.
Slag, blowholes, and paint on unfused regions were observed at the welded junctions.
在焊接处看到了夹渣，气孔及未熔透区的油漆。
2.
Any severe deficiency of welding seams surface like cracks, pores, slags is forbidden.
焊缝表面不得有裂纹,气孔,夹渣等严重缺陷.
3.
Internal defects:lack of penetration,lack of fusion,slag,gas pole,carck,overheating.
内部缺陷：未焊透、未熔合、夹渣、气孔、裂纹、过热。
4.
Methods and causes of surface slag on cast-rolling strip
铝铸轧带坯上表面夹渣的原因及其预防措施
5.
Gas Porosity and Inclusion Occur in Production of X80 Heavy Wall Thickness Pipe
X80级厚壁焊管生产中的气孔和夹渣原因分析
6.
Centrifugal casting，compact structure，free from pinhole porosity and slag，smooth surface and even wall thickness.
高速离心铸造,组织致密,无砂眼、夹渣，表面光滑、壁厚均匀。
7.
Hence lack of fusion and slag would exist at the weld root and create a large initial crack condition.
因而未熔透及夹渣存在于焊缝棍部，并造成大的初始裂纹条件。
8.
Conclusion The reason is that waste water was discharged before the precipitation.
结论废水未经沉淀，夹渣排放；某稀土厂废水是污染负荷的主要因子。
9.
Steel cutting surface or shear surface should have no cracks, slag, stratification and the lack of greater than 1 mm Prism.
钢材切割面或剪切面应无裂纹、夹渣、分层和大于1?的缺棱。
10.
Analysis on Entrapped Slag Defect of Cast Steel Wheel Poured Continuously by Bottom Pouring Ladle
用底注包连续浇注铸钢车轮产生夹渣缺陷的分析
11.
Dirty steel due to entrapment of slag or pieces of refractory.
因夹杂炉渣或耐火材料颗粒而造成的不纯净钢。
12.
AN INVESTIGATION OF MECHANISM ON THE REMOVAL OF OXIDE INCLUSIONS DURING ESR PROCESS
电渣重熔过程中氧化物夹杂去除机理的探讨
13.
Control of Content and Composition of Nonmetallic Inclusion in ESR Steel
电渣重熔钢中非金属夹杂物含量及成分的控制
14.
BEHAVIOR OF NON-METALLIC INCLUSIONS IN AN ELECTRIC RESISTANCE ALLOY DURING ESR
非金属夹杂物在电渣重熔电热合金时的行为
15.
Experimental Study on 12CaO·7Al_2O_3 Base Refining Slag of Desulfurizaiton and Removal Inclusion
12CaO·7Al_2O_3基无氟精炼渣脱硫及去除夹杂物实验研究
16.
Study on Non-Metallic Inclusions in Maraging Steel Produced by Electroslag Remelting Process
电渣重熔马氏体时效钢中的非金属夹杂物研究
17.
INFLUENCE OF CASTING POWDER TO SURFACE INCLUSIONS OF MEDIUM PLATE
连铸保护渣性能对中板表面夹杂缺陷的影响
18.
A Study on Kinetics of TiO_2 Inclusion Absorbed by Mold Fluxes
结晶器保护渣吸收TiO_2夹杂物的动力学研究