1) propylene ester
丙烯乙酯
2) ethylacrylate
丙烯酸乙酯
1.
The microstructure of methyl methacrylate(MMA) and ethylacrylate(EA) copolymer prepared by radiation polymerization was studied by 1H NMR,13CNMR,DEPT,gHMBC and gHSQC NMR spectroscopy.
用1H NMR,13C NMR,DEPT,gHMBC和gHSQC等一维、二维谱研究了γ射线辐射引发聚合的甲基丙烯酸甲酯(MMA)与丙烯酸乙酯(EA)共聚物的微观化学结构并作了归属。
2.
Irradiation of ethylacrylate(EA) in air by 60Co at dose rate>15 Gy/s gave three peroxide compenents in different contents depending on the dose rate used.
丙烯酸乙酯经在空气下６０Ｃｏγ辐照后，剂量率在１５Ｇｙ／ｓ以上时可形成３种过氧化物组份，各组份的分布随剂量率的不同而异；当剂量率为１０Ｇｙ／ｓ时，只形成单一的相当于第２组份的过氧化物。
3) ethyl acrylate
丙烯酸乙酯
1.
Synthesis and properties of poly(methylsiloxane) modified by ethyl acrylate;
丙烯酸乙酯改性硅油的合成和性能研究
2.
Study on synthesis and application of graft copolymerization of vinyl acetate and ethyl acrylate;
淀粉与乙酸乙烯酯-丙烯酸乙酯的合成与应用研究
3.
Study of kinetic of emulsion copolymerization of methyl methacrylate/ethyl acrylate;
甲基丙烯酸甲酯-丙烯酸乙酯乳液共聚动力学研究
4) 2-Propenyl ethanoate
乙酸烯丙酯
5) polypropylene/ethylene vinyl acetate
聚丙烯/乙烯-乙酸乙烯酯
6) vinyl acrylate
丙烯酸乙烯酯
补充资料：丙烯酸乙酯
CH2=CHCOOC2H5 分子量 100.11
无色透明液体，有辛辣刺激气味。 密度0.9405g／cm3。凝固点一72℃。沸点99．8℃。 闪点15．56℃(开杯)。折射率帛1．404。溶于水、乙醇、乙醚。久贮能聚合，热、光及过氧化物能增加其聚合速度。有时加入0.01％ 4-甲氧基苯酚作稳定剂。易燃。遇高热、明火、氧化剂有引起燃烧的危险。与氯磺酸反应剧烈。爆炸极限1．8％(下限)。
主要用作聚合物的单体。如用于生产聚丙烯酸乙酯，作为皮革的防裂剂和涂料的基液。用于生产丙烯酸乙酯-氯乙基乙烯基醚共聚物，作为耐热、耐油合成橡胶的主要组成。用于生产丙烯酸乙酯-乙烯共聚物，作为热熔性粘合剂的主要组成。另外还大量用作纸张浸渍剂、涂料防护剂等。
无色透明液体，有辛辣刺激气味。 密度0.9405g／cm3。凝固点一72℃。沸点99．8℃。 闪点15．56℃(开杯)。折射率帛1．404。溶于水、乙醇、乙醚。久贮能聚合，热、光及过氧化物能增加其聚合速度。有时加入0.01％ 4-甲氧基苯酚作稳定剂。易燃。遇高热、明火、氧化剂有引起燃烧的危险。与氯磺酸反应剧烈。爆炸极限1．8％(下限)。
主要用作聚合物的单体。如用于生产聚丙烯酸乙酯，作为皮革的防裂剂和涂料的基液。用于生产丙烯酸乙酯-氯乙基乙烯基醚共聚物，作为耐热、耐油合成橡胶的主要组成。用于生产丙烯酸乙酯-乙烯共聚物，作为热熔性粘合剂的主要组成。另外还大量用作纸张浸渍剂、涂料防护剂等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。