2) initial corrosion
初期腐蚀
1.
Influence of Cl~- concentration on the initial corrosion behavior of 2A12 aluminum alloy
Cl~-含量对2A12铝合金初期腐蚀行为的影响
2.
With measuring and analyzing corrosion morphology,potential and EIS,the initial corrosion of aluminum alloys in marine atmosphere and correlation of simulated marine atmosphere accelerated corrosion test and outfield corrosion test were studied.
通过对模拟海洋大气加速腐蚀试验和外场暴露试验中的LY12铝合金初期腐蚀形貌、电位和交流阻抗等的测量和分析,研究铝合金在海洋大气环境下的初期腐蚀行为,并考察加速腐蚀试验结果和外场暴露试验结果的相关性。
3.
Series of accelerated corrosion tests were conducted in simulated marine atmosphere to study initial corrosion of LY12 aluminum alloy(corresponds to USA 2024) at different humidity.
根据表面带Cl-的LY12铝合金在模拟海洋大气环境中的腐蚀形貌、增重、最大点蚀深度以及腐蚀体系的自腐蚀电位、交流阻抗等变化,分析相对湿度对其初期腐蚀行为的影响。
3) incipient decay
初期腐朽
1.
Fungi can cause dramatic decreases in strength properties during incipient decay in wood, because they can rapidly cause structural failure, even though the weight loss is minimal.
生物培养和显微镜观察被认为是目前唯一权威的用来检测和评估木材初期腐朽的方法,但这些方法很难对木材的初期腐朽进行快速、准确地评估。
4) incipient decay
初期腐烂
5) Early Ming-Dynasty s Surge against Corruption
明初的整治腐败
6) incipient decay
初期腐朽(林)
补充资料：初期复苏
初期复苏
basic life support,BLS
详见“心肺复苏”。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条