1) piercing and shaping die
冲孔成形
2) forming piercing
成形冲孔
1.
By analyzing the working process of leaking plate forming piercing compound die,the broken reasons of small convex die are found out.
通过对漏盘成形冲孔复合模工作过程的分析,找出了小凸模折断的原因,通过对小凸模采用全行程导向保护,改善了小凸模的工作条件,保证了模具的正常使用。
3) shaping and piercing die
成形冲孔模
4) side-forming punching die
侧成形冲孔模
1.
The side-forming punching die for hot blast cover with double convex boss;
热风罩立边双凸台侧成形冲孔模
5) percussive grabbing boring
冲抓成孔
1.
The paper sketches the course of research and development of "CG percussive grabbing boring equipment with casing",composition and specification of equipment;analyzed construction technology of full-casing cast-in-place pile,bitten piles and replacement stone column;sums up the field cases and development prospect.
简述了国家重点新产品"CG型全套管冲抓成孔设备"的研发历程,以及设备的组成、特点和参数;分析了全套管灌注桩、咬合桩、置换桩的施工工艺及特点;总结了该设备的应用实例和发展前景。
6) boring(ramming)hole
钻(冲)成孔
补充资料:主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广(硬质、软质、聚合物等),成型条件各有不同,从熔融至分
解之温度范围很小,尤须注意加热温度。
2. 附着水分少,但成型周期尽可能减少(50℃~60℃热风干燥)。
3. 成型机方面,与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹,故射出操作后,柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高,特别注意熔融情形。第二级加热温度较高,且尽可能使成形周
期缩短,比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高,故采用油加热的成形机较适当。
2. 吸湿性大,必须充分干燥。水分对成型品的品质影响甚大(80℃热风干燥约5~6小时)。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE,但成形温度必须较高。熔融温度170℃,超过190℃则流动性大增,则毛边增加,
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小,但若有些微之水分存在则成型品产生其它色泽或气泡,故必须密封
干燥同时成形时也须预备干燥(120℃之温度4小时)。
2. 加热温度超过320℃时则产生热分解,成品变色,故特别注意温度调节,又成型时的温度调节也非常重要,须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜(130℃~135℃,1小时程度为准)。