2) erosion resistant
耐冲蚀的
3) slurry erosion
砂浆冲蚀
1.
Two different HVOF spray systems were used to prepare six WC–10Co–4Cr coatings on 0Cr13Ni5Mo stainless steel using three commercial powders, and the slurry erosion behavior of coatings and the substrate was investigated on a self-manufactured slurry pot erosion tester.
以2种不同的HVOF喷涂系统和3种商用粉末在0Cr13Ni5Mo基材上喷涂6种WC–10Co–4Cr涂层,用自行研制的料浆罐冲蚀设备对涂层和基材的砂浆冲蚀行为进行了研究,分析了显微结构和显微硬度对涂层冲蚀性能的影响及涂层冲蚀后的表面形貌。
4) erosion sand plug
冲蚀砂柱
5) sand blast erosion
喷砂冲蚀
6) erosive wear resistance
耐冲蚀性
1.
The phase structure and microstructure of the laser clad coating were analyzed by XRD and SEM,and the erosive wear resistance of 16Mn steel and the laser clad coating was studied in different medium.
采用 CO_2连续波激光器在16Mn 钢基材表面进行 Ni 基合金熔覆处理,采用 XRD、SEM 等分析了熔覆层的相组成和微观结构,在不同的介质中研究了16Mn 钢基和合金熔覆层的耐冲蚀性。
补充资料：冲蚀
冲蚀
erosion corrosion
ehongsh-冲蚀(erosion corrosion)金属材料表面与腐蚀流体冲刷的联合作用，而引起材料局部的金属腐性。在发生这种腐蚀时，金属离子或腐蚀产物因受高速腐蚀流体冲刷而离开金属材料表面，使新鲜的金属表面与腐蚀流体直接接触，从而加速了腐蚀过程。若流体中悬浮较硬的固体颗粒，则将加速材料的损坏。一般说来，流体的速度愈高，流体中悬浮的固体颗粒愈多、愈硬，冲刷腐蚀速度愈快。腐蚀介质流动速度又取决于流动方式:层流时，由于流体的粘度，在沿管道截面有一种稳态的速度分布;湍流时，破坏了这种稳态速度分布，这不仅加速了腐蚀剂的供应和腐蚀产物的迁移，而且在流体与金属之间产生切应力，能剥离腐蚀产物，从而加大了冲蚀速度。因此，在管道的拐弯处及流体进入管道或贮罐处容易产生这种破坏。另外，金属表面成膜的特征也可以影响冲蚀速度。硬的、致密的、连续的、粘附性强的膜冲蚀速度小，反之则大。抑制或减少冲蚀的措施是:选择耐蚀性和耐磨性好的材料;改变腐蚀环境如添加缓蚀剂，过滤悬浮固体粒子，降低温度，减小流速和湍流;采用栖牲阳极作阴机保护等。 (1陈树俊l)