1) gahnospinel
镁锌尖晶石
2) magnesia spinel
镁尖晶石
1.
Taking fused magnesia, fused spinel and sintered spinel as raw material and titania as additives,the specimen of magnesia spinel bricks were prepared through the production processes of mix, mould pressing and sintering.
以电熔镁砂、电熔尖晶石和烧结尖晶石为主要原料,铁鳞和钛白粉为添加剂,经过混合,半干法成型,高温烧成等制备工艺制成了新型镁尖晶石砖,并对其性能进行了研究。
4) magnesia-alumina spinel
镁铝尖晶石
1.
Study on preparation of magnesia-alumina spinel additive and its performances of catalytic olefin reduction;
镁铝尖晶石的制备及其催化降烯烃性能研究
2.
Synthesis of magnesia-alumina spinel refractories;
镁铝尖晶石质耐火材料的合成
3.
Preparation of magnesia-alumina spinel and its application in catalytic reaction;
镁铝尖晶石的制备及在催化反应中的应用
6) Magnesia alumina spinel
镁铝尖晶石
1.
The fused magnesia,magnesia alumina spinel and α-Al2O3 were put in the ground substance for developing the stability of thermal shock.
以优质电熔镁砂、烧结镁铝尖晶石为主要原料,采用纸浆废液作为结合剂研究镁质复合滑板材料。
2.
Thermodynamic analysis and hot condition experiment were used to study the effects of temperature of molten steel and mass fraction of carbon on the corrosion of magnesia alumina spinel refractory,and the corrosion mechanism was discussed.
根据热力学分析和热态实验研究了钢水温度及其碳质量分数对镁铝尖晶石质耐火材料侵蚀的影响,并探讨了耐火材料的侵蚀机理。
补充资料：半透明烧结镁铝尖晶石陶瓷
分子式：
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。