1) magnesium-spinel-carbon brick
镁-尖晶石-碳
2) magnesia-spinel carbon refractories
镁尖晶石碳
1.
Slag corrosion resistance of microporous magnesia-spinel carbon refractories was studied using periclase-spinel microporous aggregate,fused magnesia,fused spinel,micro alumina powder as starting materials.
以方镁石-尖晶石微孔陶瓷、电熔镁砂为骨料,以电熔镁砂细粉、鳞片石墨、金属铝粉为基质材料,以酚醛树脂为结合剂制备了含微孔陶瓷骨料的镁尖晶石碳试样。
3) Periclase spinel carbon
方镁石尖晶石碳
4) aluminum-spinel-carbon
铝镁尖晶石碳
5) magnesia spinel
镁尖晶石
1.
Taking fused magnesia, fused spinel and sintered spinel as raw material and titania as additives,the specimen of magnesia spinel bricks were prepared through the production processes of mix, mould pressing and sintering.
以电熔镁砂、电熔尖晶石和烧结尖晶石为主要原料,铁鳞和钛白粉为添加剂,经过混合,半干法成型,高温烧成等制备工艺制成了新型镁尖晶石砖,并对其性能进行了研究。
6) aluminium magnesium-aluminium spine carbon unfired bricks
铝镁铝尖晶石碳不烧砖
补充资料：半透明烧结镁铝尖晶石陶瓷
分子式：
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。