1) Multiple emulsion
复合型乳剂
2) complex demulsifier
复合型破乳剂
1.
To solve the problem of high FeS in waste water from some electric desalters,a novel complex demulsifier has been developed.
为解决油田和炼油厂的电脱水/脱盐器排水中出现的颗粒状FeS问题,研制了复合型破乳剂,在破乳剂用量10μg/g,电场强度800 V/cm,温度120℃,注水量5%条件下,排水中FeS降低了99%以上,排水含油降低了60%。
3) Hybrid emulsifier
复合型乳化剂
1.
Hybrid emulsifier with excellent performance and waterborne epoxy emulsion composed of small emulsion particles are formulated.
制备了相容性优良、反应活性适当的水性环氧固化剂,合成了具有优异性能的复合型乳化剂和乳液粒径较小的水性环氧乳液,得到了耐水、耐碱性能优异的涂膜,并讨论了影响水性环氧涂料性能的因素。
4) multiple emulsion
复合乳剂
5) complex emulsifier
复合乳化剂
1.
Effects of emulsifying temperature and adding time of complex emulsifier into the liquid rosin system on emulsification efficiency,sizing performance of the third-grade rosin based cationic dispersed rosin size were investigated in this paper.
采用常压逆转工艺制备出了性能优良的阳离子微粒乳化中性分散松香胶,对制备过程中乳化温度、复合乳化剂的加入时间进行了探讨,实验结果表明,在综合考虑操作成本与乳化效果的前提下,乳化温度以140℃为宜,复合乳化剂的加入时间以20m in为宜。
2.
The effects of various amount of oxidative agent/reductive agent, reaction temperature, complex emulsifier on the monomer conversion intrinsic viscosity and emulsion stability are studied.
结果表明 :采用氧化还原引发剂可以使聚合反应低温快速进行 ,过量的还原剂起阻聚或缓聚的作用 ,采用复合乳化剂体系可提高聚合反应速度和乳液的稳定性 ,合成的共聚物为无规共聚
3.
Copolymer of acrylamide and ammonium acrylate was prepared by inverse emulsion polymerization,with liquid paraffin as continuous phase,acrylic acid and acrylamide aqueous solution as dispersing phase,N,N′-methylene-bisacrylamide as cross-linking agent,Span-80 and Tween-80 as complex emulsifier,and ammonium persulfide as initiating agent.
采用反相乳液聚合法,以液体石蜡为连续相、丙烯酰胺和丙烯酸水溶液为分散相、N,N′-亚甲基双丙烯酰胺为交联剂、过硫酸铵为引发剂,制备了丙烯酰胺(AM)-丙烯酸铵(AA)共聚物;考察了引发剂含量、单体AM含量、复合乳化剂Span-80与Tween-80的配比、聚合体系pH、聚合温度、油水比等对AM-AA共聚物性能的影响。
6) mixed emulsifier
复合乳化剂
1.
Phospholipids as stabilizing agent in mixed emulsifiers used in emulsion explosive have been reported, but the amount is less.
为提高乳化炸药的稳定性,同时降低SP80在乳化炸药中的用量,达到降低生产成本的目的,本论文研究了磷脂及改性磷脂与乳化剂SP80复配制备的复合乳化剂的性能,并将获得的含有改性磷脂的复合乳化剂应用在乳化炸药的制备。
补充资料：非离子型高分子破乳剂
分子式：
CAS号：
性质：链节中不带离子基团的高分子破乳剂。非离子型石油破乳剂与离子型石油破乳剂根本不同，它在水中不解离，而靠氧乙烯链作为亲水部分，其他为疏水部分。是目前研究和应用最广泛的一大类。例如聚氧乙烯聚氧丙烯烷基醇(或苯酚)醚、聚氧乙烯聚氧丙烯丙二醇醚、聚氧乙烯烷基苯酚甲醛树脂、聚氧乙烯聚氧丙烯多乙烯多胺醚、聚氧乙烯聚氧丙烯酚胺树脂等。
CAS号：
性质：链节中不带离子基团的高分子破乳剂。非离子型石油破乳剂与离子型石油破乳剂根本不同，它在水中不解离，而靠氧乙烯链作为亲水部分，其他为疏水部分。是目前研究和应用最广泛的一大类。例如聚氧乙烯聚氧丙烯烷基醇(或苯酚)醚、聚氧乙烯聚氧丙烯丙二醇醚、聚氧乙烯烷基苯酚甲醛树脂、聚氧乙烯聚氧丙烯多乙烯多胺醚、聚氧乙烯聚氧丙烯酚胺树脂等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条