1) tarnish film
锈膜，氧化膜
2) tarnish film
锈[氧化]膜
3) film rust
锈膜
4) film of oxide
氧化物膜;氧化膜
5) oxide film
氧化膜
1.
Effect of annealing technology on oxide film and specific capacity of aluminum foils for low voltage electrolytic capacitors;
退火工艺对低压铝箔氧化膜和比电容的影响
2.
Effect of aluminium alloy outer oxide films on the loss of electrode during spot welding;
铝合金表面氧化膜对点焊电极磨损的影响
3.
Influence of applied stress on cracking and apalling of oxide film in room temperature;
外力对常温氧化膜开裂和剥落行为的影响
6) oxide scale
氧化膜
1.
Spalling behavior of oxide scale of high-speed steel roll;
热轧高速钢轧辊氧化膜的剥落行为分析
2.
The oxide scales were examined by SEM,X-ray diffraction and ESA.
X射线衍射、扫描电镜和能谱分析表明,K447氧化膜分为3层:外层是疏松的Cr2O3和TiO2的混合物,并含有少量的N iO及N iCr2O4尖晶石;中间层是Cr2O3;内氧化物层是A l2O3,并含有少量TiN。
3.
This oxide scale composed of pure Al_2O_3 has a good adhesion ability,no spallation was found during the high temperature oxidation.
通过最小二乘拟合得到的合金氧化动力学模型近似遵循4次方规律,并在高温氧化过程中,合金能够生成单一的Al2O3氧化膜,而且氧化膜的粘附性好,不易脱落。
补充资料：氧化膜
分子式：
CAS号：
性质： 活性溶解着的金属进入钝态后，在金属表面上存在着一成相的保护膜。这层膜为氧化膜，亦称钝化膜，它阻滞腐蚀的阳极过程，从而使腐蚀速度显著降低。氯离子是活性阴离子，它能破坏钝化膜，使钝态的金属重新活化。因此研究钝化膜的生长和破坏、膜的性质和结构、膜和金属的溶解，对于了解金属的腐蚀行为至关重要。