1) silica membranes
氧化硅膜
1.
The ordered silica membranes supported by α-alumina hollow fibers was prepared from copolymer plutonic P123 and TEOS.
本文介绍了在α-Al2O3中空纤维载体上制备担载有序氧化硅膜的方法。
2) silicon oxidizing film
硅氧化膜
4) silica membrane
二氧化硅膜
1.
Methyl-modified silica membranes were prepared by acid catalysed co-hydrolysis and condensation reaction of tetra-ethylortho-silicate(TEOS) and methyl-tri-ethoxy-silane(MTES) in ethanol and characterized by TGA,FTIR and gas permeation.
用甲基三乙氧基硅烷(MTES)代替部分正硅酸乙酯(TEOS)作为前驱物,通过共水解缩聚反应可制得甲基修饰的二氧化硅膜。
2.
Microporous silica membranes on Υ-Al2O3/α-Al2O3 porous supports were prepared by a sol-gel process, and characterized by IR, TG, FE-SEM,N2 adsorption as well as gas permeation.
利用溶胶-凝胶法在Υ-Al2O3/α-Al2O3多孔支撑体上合成了微孔二氧化硅膜,并用IR、TG、FESEM、N2吸附以及气体渗透等手段对二氧化硅膜进行了研究。
3.
The surface wettability,surface structure and water absorbed amount of the silica membranes were investigated.
以正硅酸乙酯(TEOS)、甲基三乙氧基硅烷(MTES)为硅源,硝酸为催化剂,制备了甲基修饰的二氧化硅膜,研究了MTES改性二氧化硅膜的表面润湿性与表面结构的关系以及MTES改性二氧化硅膜的吸水率。
5) silica film
二氧化硅膜
1.
Synthesis of silica film using tetraethylorthosilicate;
利用正硅酸乙酯制备二氧化硅膜
6) silicon dioxide films
二氧化硅薄膜
1.
FT-IR study of silicon dioxide films fabricated by rapid thermal oxidation;
快速热氧化制备二氧化硅薄膜的红外研究
补充资料：硅-氧化钠-五氧化二钒系湿敏材料
分子式：
CAS号：
性质：一种感湿体材料。主晶相为硅粉，氧化钠和五氧化二钒起助熔体和黏结作用。680℃固相烧结法制取。游离硅粒保证瓷体的低电阻率，氧化钠和五氧化二钒有利于吸收水分，受潮后使硅粒之间的电阻值显著下降。材料响应速度慢，吸湿时间≥5min，脱湿时间≥l0min，宜用于中湿和湿度变化不太快的场合。制作的湿敏元件体积小、机械强度好、阻值范围可调，工作寿命长。