1) excess convexity
过高(焊缝)
2) welding line over-burn
焊缝过烧
3) weld reinforcement
焊缝余高
1.
This article introduced weld reinforcement importance to SSAW pipe,effect of weld reinforcement to weld mechanical property and to SSAW pipe anti-corrosion.
介绍了螺旋埋弧焊管焊缝余高的重要性、焊缝余高对焊缝力学性能的影响以及余高对螺旋埋弧焊管防腐的影响。
2.
Produced stress concentration if weld reinforcement too large for submerged arc welding,so it should be control.
埋弧自动焊焊缝余高过大会对压力容器产生应力集中的影响,因此应加以控制。
6) transition layer weld
过渡层焊缝
1.
The results show that the tensile strength of the joints was 512 MPa,and the microstructure transition between clad metal/heat affected zone/transition layer weld was mild,and biphase proportion of austenite and ferrite was in the required range.
对SAF2205/16MnR双相不锈钢复合板进行了焊接,基层采用手工电弧焊,以E5015焊条为填充材料,过渡层及覆层采用钨极氩弧焊,以ER2209焊丝为填充材料;对焊接接头进行了拉伸试验,利用扫描电镜、光学显微镜及X射线衍射仪等分析了接头过渡层焊缝及其熔合区域的显微组织及物相组成。
补充资料：过烧
分子式：
CAS号：
性质：制品超过烧成温度称为过烧。过烧的制品易出现变形、尺寸不符合要求、坯体或釉面有气泡等。瓷体内部液相(玻璃相)增加、晶界变宽、易出现晶体异常长大、晶粒不均匀、致密度和强度下降等。导致过烧的原因是烧成温度过高，保温时间太长。窑内温度不匀也会造成局部过烧。
CAS号：
性质：制品超过烧成温度称为过烧。过烧的制品易出现变形、尺寸不符合要求、坯体或釉面有气泡等。瓷体内部液相(玻璃相)增加、晶界变宽、易出现晶体异常长大、晶粒不均匀、致密度和强度下降等。导致过烧的原因是烧成温度过高，保温时间太长。窑内温度不匀也会造成局部过烧。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条