1) inoculant alloy
球化剂合金
2) nodulizing alloy
球化合金
1.
The requirements of ductile iron on spheroidization effect,matrix state,and decreasing tendency of chill,shrinkage and dispersed shrinkage can be satisfied by adjusting the chemical composition of nodulizing alloy.
调整球化合金的化学成分,可以满足各种牌号铸态球墨铸铁对球化效果、基体状态和减少白口与缩孔、缩松倾向的要求。
3) mixed nodulizer
混合球化剂
1.
The effects of the mixed nodulizer,suspension pouring process and the trace element on the graphite morphology were aiscussed in heavy section ductile iron by using the simulating test set.
试验结果表明 :运用混合球化剂、悬浮浇注工艺和加入微量元素 Sn、Sb,可以防止组织中的石墨畸变 ,细化石墨球和提高球化级
4) catalyzer alloy
催化剂合金
1.
At HTHP(High Temperature High Pressure),large quantity of C atom or aggregate of graphite material dissolves into catalyzer alloy,while returning to normal temperature and pressure,the saturated C will separate from alloy crystal lattice forming graphite crystal in alloy,becoming re-crystallized graphite.
石墨材料在高温高压条件下,大量的C原子和原子团溶解于催化剂合金中,当回到常温常压下,过饱和的C会从合金晶格中析出来,形成的石墨晶体存在于合金中,成为重结晶石墨。
2.
At HTHP(high temperature high pressure),large quantity of C atom or aggregate of graphite material dissolves into catalyzer alloy,while returning to normal temperature and pressure,the saturated C will separate from alloy crystal lattice forming graphite crystal in alloy,becoming re-crystallized graphite.
石墨材料在高温高压条件下,大量的C原子和原子团溶解于催化剂合金中,当回到常温常压下,过饱的C会从合金晶格中析出来,形成的石墨晶体存在于合金中,成为重结晶石墨。
5) alloy catalyst
合金催化剂
1.
Orthogonal test on a new alloy catalysts for xylose hydrogenation to xylitol;
新型合金催化剂用于木糖加氢制木糖醇的正交试验研究
2.
The manufacturing method of a new alloy catalyst for hydrogenation of furfural to 2 methyfuran in gas phase was developed.
研究糠醛气相加氢制 2 -甲基呋喃的合金催化剂的制备方法 。
3.
he catalytic behavior of ultra-fine amorphous Ni-B alloy catalysts for benzene hydrogenation was studied.
非晶态超微粒子镍合金催化剂的研究──Ⅱ。
6) Rare-earth compound nodularizer
稀土复合球化剂
补充资料：球化剂
nodulizer：是使铁水中石墨在凝固时成球状析出的添加剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。