1) Molybdenum alloy catalysts
钼合金催化剂
2) molybdenum polymerization catalyst
钼系聚合催化剂
4) catalyzer alloy
催化剂合金
1.
At HTHP(High Temperature High Pressure),large quantity of C atom or aggregate of graphite material dissolves into catalyzer alloy,while returning to normal temperature and pressure,the saturated C will separate from alloy crystal lattice forming graphite crystal in alloy,becoming re-crystallized graphite.
石墨材料在高温高压条件下,大量的C原子和原子团溶解于催化剂合金中,当回到常温常压下,过饱和的C会从合金晶格中析出来,形成的石墨晶体存在于合金中,成为重结晶石墨。
2.
At HTHP(high temperature high pressure),large quantity of C atom or aggregate of graphite material dissolves into catalyzer alloy,while returning to normal temperature and pressure,the saturated C will separate from alloy crystal lattice forming graphite crystal in alloy,becoming re-crystallized graphite.
石墨材料在高温高压条件下,大量的C原子和原子团溶解于催化剂合金中,当回到常温常压下,过饱的C会从合金晶格中析出来,形成的石墨晶体存在于合金中,成为重结晶石墨。
5) alloy catalyst
合金催化剂
1.
Orthogonal test on a new alloy catalysts for xylose hydrogenation to xylitol;
新型合金催化剂用于木糖加氢制木糖醇的正交试验研究
2.
The manufacturing method of a new alloy catalyst for hydrogenation of furfural to 2 methyfuran in gas phase was developed.
研究糠醛气相加氢制 2 -甲基呋喃的合金催化剂的制备方法 。
3.
he catalytic behavior of ultra-fine amorphous Ni-B alloy catalysts for benzene hydrogenation was studied.
非晶态超微粒子镍合金催化剂的研究──Ⅱ。
6) Co Mo、Ni Mo catalysts
钴钼、镍钼催化剂
补充资料：钼钴镍催化剂
分子式：
CAS号：
性质：一种用于炼油的加氢精制催化剂。深蓝色。片状或1.2～2.5mm的小球状。堆积密度0.86～1.0g/cm3。氧化铝为载体。活性组分大致含氧化镍2.6%～3.2%，氧化钴1.3%～1.9%，三氧化钼15%～18%。活性高。反应温度低。稳定性好。强度高。寿命长。脱氮脱硫性能比钴钼和镍催化剂好。常用于汽油、柴油、煤油的加氢精制。常压柴油和减压柴油的加氢脱硫。
CAS号：
性质：一种用于炼油的加氢精制催化剂。深蓝色。片状或1.2～2.5mm的小球状。堆积密度0.86～1.0g/cm3。氧化铝为载体。活性组分大致含氧化镍2.6%～3.2%，氧化钴1.3%～1.9%，三氧化钼15%～18%。活性高。反应温度低。稳定性好。强度高。寿命长。脱氮脱硫性能比钴钼和镍催化剂好。常用于汽油、柴油、煤油的加氢精制。常压柴油和减压柴油的加氢脱硫。