The Al2O3 coating acts as load support layer, the CrN coating was deposited on top of the Al2O3 coating by radio frequency magnetron sputtering technique.
在LY12CZ铝合金表面采用微弧氧化技术制备了氧化铝陶瓷膜,使用砂纸打磨抛光去除表面疏松层,并把氧化铝陶瓷薄膜当着承载层,采用射频磁控溅射的物理气相沉积法在其表面制备氮化铬改性层。
5) chromium nitride
氮化铬
1.
At present, chromium nitride powderis produced by carbon thermal reduction, which has some shortcomings, for example,the chromium nitride powder has low purity.
氮化铬粉体具有很多优异的性能，如硬度高、耐酸碱腐蚀性好、化学稳定性高、耐磨性能好、高熔点等，使其在磁学、电子工业、耐高温结构陶瓷等多方面得到广泛应用。
2.
Owing to the thermal stability, excellent wear resistance and good corrosion resistance, chromium nitride coating is regarded as an alternative in machining applications.
氮化铬陶瓷涂层具有低的磨擦系数、高的硬度、良好的热稳定性和抗腐蚀性,被认为是最有希望的 TiN替代材料之一。
6) Cr penetration and nitriding
渗铬氮化
补充资料：氮化铬
分子式：CrN
CAS号：
性质：常用作薄膜涂层。具有高的硬度和良好的耐磨性，是一种很受重视的耐磨涂层。用空心阴极离子镀制备的氮化铬膜具有Cr+Cr2N两相组织，晶粒度为20～70nm，硬度为HV22GPa。经真空退火后，能提高到HV35.4GPa。其耐磨性优于CrC膜。反应溅射法氮化铬膜能得到Cr+Cr2N或单相CrN两种组织，其硬度均在HV20～25GPa(块体CrN硬度HV11GPa)。
CAS号：
性质：常用作薄膜涂层。具有高的硬度和良好的耐磨性，是一种很受重视的耐磨涂层。用空心阴极离子镀制备的氮化铬膜具有Cr+Cr2N两相组织，晶粒度为20～70nm，硬度为HV22GPa。经真空退火后，能提高到HV35.4GPa。其耐磨性优于CrC膜。反应溅射法氮化铬膜能得到Cr+Cr2N或单相CrN两种组织，其硬度均在HV20～25GPa(块体CrN硬度HV11GPa)。