1) bursting stress
爆裂应力
2) strain burst
应变爆裂
3) burst pressure
爆裂压力
1.
Comparative study on pipeline burst pressure model and developed residual strength evaluation methods
压力管道爆裂压力模型比较研究和改进的剩余强度评价方法
5) thermal,spalling
热爆裂(由于制品中存在温度差产生应力而破裂)
6) stress crack
应力开裂
1.
The mechanism of stress cracking and find what the key impact to this problem is researched.
通过对应力开裂机理进行研究和讨论,找出了影响碳酸饮料包装瓶应力开裂的因素,提出了解决思路和方法,并在生产实践中对制瓶工艺进行优化,最终解决了碳酸饮料包装瓶的应力开裂技术难题。
2.
The mechanical properties and stress crack properties of PC/ABS and PC/ABS/PE g MAH blends were studied.
研究了聚碳酸酯与ABS(PC/ABS)及PC/ABS与马来酸酐接枝聚乙烯共聚物 (PC/ABS/PE -g-MAH)共混体系的力学性能和应力开裂性能。
3.
The paper summarizes the causes of the internal stress in injected part and the influencing factors, discusses the measures to eliminate the stress crack, determines the optimum process condition by the orthoqonal method and intnxluces the heat treatment technology and the method of stress inspection.
论述注塑件内应力产生的原因和影响因素,研究消除应力开裂的有效措施,用正交设计法确定最佳注射工艺,介绍热处理工艺和应力检验方法。
补充资料：爆裂
爆裂
bursting
b0Olie爆裂(b盯sting)管材生产中穿透管壁的突发性纵向开裂，通常出现在空拔管中。因为空拔后管材外表面存在较大的切向拉伸残余应力(见管材冷援变形原理)。管壁厚和气温低时发生空拔爆裂倾向更大。为防止纵裂缺陷，空拔时减径量不能过大，连拔道次要少，拔后应及时烘烤或退火。为防止钢管爆裂也可采用滚模拔制。(见管材冷轧冷拔) (李连诗)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。