1) tungsten carbide stud
柱状碳化钨块
2) tungsten carbide slug
碳化钨块
3) block carbide
块状碳化物
1.
The result shows that the early failure of large box moving die results from large block carbides,composition segregation and coarse microstructure.
结果表明,材料中存在锋利、多角块状碳化物、成分偏析、组织粗大,三者共同作用导致大型箱体动模早期失效。
4) nickel-tungsten-tungsten carbide
镍-钨-碳化钨
5) tungsten carbide
碳化钨
1.
Thermal mechanical alloying synthesis of tungsten carbide-metal composites;
碳化钨-金属复合材料的热机械合金化合成
2.
Electrochemical reduction behavior of α-nitronaphthalene on tungsten carbide catalysts with meso-porosity;
α-硝基萘在介孔结构碳化钨催化剂上的电化学还原行为
3.
Plasma enhanced chemical vapour deposition Nanocrystalline tungsten carbide thin films;
化学气相沉积制备碳化钨纳米晶薄膜
6) WC
碳化钨
1.
Isomerization Reaction of n-Pentane over WC Catalyst;
碳化钨催化剂上正戊烷异构化反应
2.
Study of Particle Size Testing of Superfine WC Powder;
超细碳化钨粉末粒度测试方法的研究
3.
Preparation of WC Powder by the Combination of Spray-drying and Fixed Bed Technology;
喷雾干燥-固定床法制备碳化钨粉末
补充资料：碳化钨
化学式WC。为黑色六方晶体，有金属光泽，硬度与金刚石相近，为电、热的良好导体。熔点2870℃, 沸点6000℃，相对密度 15.63(18℃)。碳化钨不溶于水、盐酸和硫酸，易溶于硝酸－氢氟酸的混合酸中。纯的碳化钨易碎，若掺入少量钛、钴等金属，就能减少脆性。用作钢材切割工具的碳化钨，常加入碳化钛、碳化钽或它们的混合物，以提高抗爆能力。碳化钨的化学性质稳定。
在碳化钨中，碳原子嵌入钨金属晶格的间隙，并不破坏原有金属的晶格，形成填隙固溶体，因此也称填隙（或插入）化合物（见图）。碳化钨可由钨和碳的混合物高温加热制得，氢气或烃类的存在能加速反应的进行。若用钨的含氧化合物进行制备，产品最终必须在1500℃进行真空处理, 以除去碳氧化合物。碳化钨适宜在高温下进行机械加工，可制作切削工具、窑炉的结构材料、喷气发动机、燃气轮机、喷嘴等。
钨与碳的另一个化合物为碳化二钨，化学式为 W2C，熔点为2860℃，沸点6000℃,相对密度17.15。其性质、制法、用途同碳化钨。
在碳化钨中，碳原子嵌入钨金属晶格的间隙，并不破坏原有金属的晶格，形成填隙固溶体，因此也称填隙（或插入）化合物（见图）。碳化钨可由钨和碳的混合物高温加热制得，氢气或烃类的存在能加速反应的进行。若用钨的含氧化合物进行制备，产品最终必须在1500℃进行真空处理, 以除去碳氧化合物。碳化钨适宜在高温下进行机械加工，可制作切削工具、窑炉的结构材料、喷气发动机、燃气轮机、喷嘴等。
钨与碳的另一个化合物为碳化二钨，化学式为 W2C，熔点为2860℃，沸点6000℃,相对密度17.15。其性质、制法、用途同碳化钨。