1) molybdenum(tungsten)carbide
碳化钼(钨)
2) molybdenum-tungsten oxide
氧化钼钨
1.
Multielemental bimetallic molybdenum-tungsten oxide nanorods were synt hesized under mild hydrothermal conditions with the aid of Na2SO4 salt, using fr eshly prepared molybdic-tungstenic acid precipitate as precursor.
本文通过温和的水热方法,以钼钨酸沉淀作为前驱体,在Na2SO4的辅助作用下,合成了双金属多元型的氧化钼钨纳米棒,并通过TEM、SEM、XRD、EDS和PL等手段对产物进行了表征。
3) molybdenum(tungsten)nitride
氮化钼(钨)
1.
High specific surface molybdenum(tungsten)nitride(carbide)used as a new type catalystic material due to its high activity in the catalystic hydrogenation and dehydrogenation reaction are highly evaluated.
高比表面的氮化钼（钨）和碳化钼（钨）在催化加氢脱氢反应中表现出高的活性，成为催化领域中一种新型催化材料而受到重视。
4) nickel-tungsten-tungsten carbide
镍-钨-碳化钨
5) molybdenum carbide
碳化钼
1.
An investigation on the hydrodenitrogenation performance of molybdenum carbide catalyst;
碳化钼催化剂加氢脱氮性能研究
2.
Study on n-heptane isomerization on β zeolite supported molybdenum carbide catalyst;
正庚烷在β沸石负载碳化钼催化剂上的异构化研究
3.
Preparation of molybdenum carbide catalyst and its hydrodesulfurization performance for thiophene;
碳化钼催化剂的制备及噻吩加氢脱硫性能
6) molybdenum carbide
碳化钼<冶>
补充资料：碳化钼陶瓷
分子式：
CAS号：
性质：钼与碳的化合物为主要成分的陶瓷。主要有两类。(1)以碳化二钼(Mo2C)为主晶相的陶瓷。呈暗灰色。理论密度9.2g/cm3。熔点2690℃。莫氏硬度7。显微硬度1800kg/mm3(负荷50g)。弹性模量22100kg/mm2。热导率6.7×106W/(m·K)。2300℃以上分解。(2)以一碳化一钼(MoC)为主晶相的陶瓷。理论密度8.88g/cm3。熔点2700℃。一般先制成碳化钼粉末(采用钼与碳直接化合法、金属氧化物与碳的还原一化合法、气相沉积法和自蔓延高温合成法)，然后在真空或还原气氛下在碳管炉、钼丝炉、高频真空炉中进行烧结(多采用反应烧结、热压烧结和热等静压烧结)而制成。主要用作超硬工具材料、耐磨材料、发热体材料以及高温结构材料。
CAS号：
性质：钼与碳的化合物为主要成分的陶瓷。主要有两类。(1)以碳化二钼(Mo2C)为主晶相的陶瓷。呈暗灰色。理论密度9.2g/cm3。熔点2690℃。莫氏硬度7。显微硬度1800kg/mm3(负荷50g)。弹性模量22100kg/mm2。热导率6.7×106W/(m·K)。2300℃以上分解。(2)以一碳化一钼(MoC)为主晶相的陶瓷。理论密度8.88g/cm3。熔点2700℃。一般先制成碳化钼粉末(采用钼与碳直接化合法、金属氧化物与碳的还原一化合法、气相沉积法和自蔓延高温合成法)，然后在真空或还原气氛下在碳管炉、钼丝炉、高频真空炉中进行烧结(多采用反应烧结、热压烧结和热等静压烧结)而制成。主要用作超硬工具材料、耐磨材料、发热体材料以及高温结构材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条