1) surface checking
表面起网状裂纹
2) surface network cracks
表面网状裂纹
1.
The surface network cracks are obviously intergranular located at the boundaries of abnormally large prior-austenite grains.
在大方坯连铸中,经常出现的缺陷是表面网状裂纹。
3) network cracks
网状裂纹
1.
The results of microscope,SEM,TEM and EDS revealed that the particles precipitated in the pre- austenite grain boundaries will result in network cracks under sufficient stress such as thermal stress,bending and straightening stress due to uneven cooling of strand surface.
采用金相显微镜、SEM、TEM和EDS等方法,分析了因连铸板坯表面冷却不均匀引起γ→α反复相变导致碳氮化物在晶界析出,并在外力(热应力、弯曲矫直应力等)作用下产生沿晶界开裂的网状裂纹的形成机理,以及钢中[C]、Mn/S、[Al]、[V]、连铸冷却强度等对连铸板坯网状裂纹的形成和扩展的影响。
2.
For the surface network cracks in 200mm thickness slabs for pipeline and veicle frame,it is found that the carbon content,Mn/S ratio and Al,Ti,V,Nb alloy additions and continuous caster conditions are attributa- ble to the formation and propagation of surface and subsurface network cracks.
统计分析了攀钢所产管线钢、梁板钢等200mm×1300mm连铸坯表层网状裂纹的影响因素;发现钢中碳、锰硫比、合金元素(Al,Ti,V)、连铸机设备和浇注状况对其形成和扩展都有重要影响。
3.
For the surface network cracks in 200mm thickness slabs for pipeline and vehicle frame, it is found that the carbon content,Mn/S ratio and Al,Ti,V,Nb alloy additions and continuous caster conditions are attributable to the formation and propagation of surface and subsurface network cracks.
针对攀钢生产的管线钢、梁板钢等200×1300mm~2连铸坯表层出现网状裂纹,对其影响因素进行统计分析,发现钢中C、Mn／S 比和 Al、Ti、V、Nb 等合金元素及连铸机设备和浇注状况对连铸坯表层网状裂纹的形成和扩展都有重要影响。
4) surface crack
表面裂纹
1.
Preventive to surface crack of MB15 magnesium alloy Φ482 mm ingot;
MB15镁合金Φ482mm铸锭表面裂纹的预防措施
2.
Surface Cracks in TP2 Copper Tube Billets in Horizontal Continuous Casting;
TP2铜管坯水平连铸表面裂纹研究
3.
An Analysis on Surface Cracks Formation of H Beam of Nb-V Microalloying Steel BS55C;
Nb-V微合金化H型钢BS55C表面裂纹成因分析
5) surface flaw
表面裂纹
1.
The surface flaws of different sizes were introduced into SiC/BN laminated ceramics by Vickers indentation method.
采用压痕法在SiC/BN层状陶瓷试样的表面引入不同尺寸的表面裂纹,利用三点弯曲测量含裂纹试样的极限断裂应力,研究了不同尺寸的表面裂纹对层状陶瓷断裂强度的影响;根据压痕载荷-强度实验结果,测定层状陶瓷的阻力曲线,并与单相SiC陶瓷对比。
6) Surface cracks
表面裂纹
1.
Analysis of reasons for surface cracks of 42CrMo spindle;
42CrMo主轴表面裂纹形成原因的分析
2.
The cause of surface cracks of the propylene spherical tank was analyzed comprehensively.
分析了球罐产生表面裂纹的原因 ,选择合适修复方案 ,对该球罐进行了修复。
3.
Surface cracks have a very complicated stress state To give the safety of device with cracks is very difficult by normal method of stress analysis This article makes a crack adjudhement with the code of CVDA-84 to the surface cracks in the balled vessel which was inspected in 199
依据ＣＡＤＡ－８４对云南沾益化肥厂３＃液氨球罐１９９６年５月检验出的表面裂纹作出了缺陷评定