1) redox initiate polymerization
氧化还原引发聚合
2) Polymerizable photo-redox initiation system
可聚合的光氧化还原引发体系
3) N,N-Dimethyl aminoethyl metharylate (DMAEMA)
可聚合光氧化还原引发体系
4) redox initiator
氧化还原引发剂
1.
An acrylamide(AM)/potassium acrylate(AAK) copolymer with high molecular weight was prepared at room temperature by inverse emulsion polymerization using cyclohexane as solvent,SPAN80/OP10 as compound emulsifier,potassium peroxysulphate (KPS)-tetramethyl ethylene diamine (TMEDA) as redox initiator.
采用环己烷作溶剂,SPAN80/OP10为复配乳化剂,过硫酸钾(KPS)-四甲基乙二胺(TMEDA)为氧化还原引发剂,丙烯酰胺(AM)和丙烯酸钾(AAK)为原料,室温下,通过反相乳液聚合法制备了高相对分子质量AM/AAK共聚物。
2.
The copolymerization for degraded natural rubber latex with methacrylate (MA)or butylacrylate(BA) by redox initiator BPO/DMA is studied.
研究了降解天然橡胶胶乳与丙烯酸甲酯、丙烯酸丁酯的聚合,以过氧化苯甲酰 N,N 二甲基苯胺(BPO DMA)为氧化还原引发剂,考察了不同反应温度、引发剂配比、乳化剂用量及加料方式对单体转化率和接枝率的影响;用红外光谱对共聚物进行了表征。
3.
Poly(acrylic acid)/clay composite super-absorbent based on acrylic acid(AA) and clay was prepared in aqueous solution using Al2O3 as crosslinking agent and Na2S2O8-Na2SO3 as redox initiator.
以黏土、丙烯酸为原料,Al2O3为交联剂,Na2S2O8-Na2SO3为氧化还原引发剂,用水溶液聚合法合成了聚丙烯酸/黏土复合高吸水性树脂。
5) redox initiator
氧化-还原引发剂
补充资料：氧化还原引发聚合
分子式：
分子量：
CAS号：
性质：借氧化-还原体系引发剂引发的自由基聚合反应。其引发剂一般含在两个组分：一个是氧化剂；一个是还原剂。由于氧化剂与还原剂间的氧化还原反应，产生了自由基，从而引发单体聚合。常用的氧化剂有过氧化氢、过硫酸盐（钾盐或铵盐）、过氧化二苯甲酰等；还原剂有亚铁盐和其他变价金属等。引发温度低，同时速率又快。合成橡胶工业中应用最多。
分子量：
CAS号：
性质：借氧化-还原体系引发剂引发的自由基聚合反应。其引发剂一般含在两个组分：一个是氧化剂；一个是还原剂。由于氧化剂与还原剂间的氧化还原反应，产生了自由基，从而引发单体聚合。常用的氧化剂有过氧化氢、过硫酸盐（钾盐或铵盐）、过氧化二苯甲酰等；还原剂有亚铁盐和其他变价金属等。引发温度低，同时速率又快。合成橡胶工业中应用最多。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。