1) redox initiation system
氧化还原引发体系
1.
The effect of redox initiation system on St/BA/AN water-base coatings emulsion polymerization;
氧化还原引发体系对St/BA/AN水性涂料乳液聚合的影响
2.
Subsequently,by using the PS latex as seed,a mixture of butyl 4-vinylbenzenesulfonate and divinylbenzene was added and polymerized to form a relatively uniform cross-linking shell surrounding the PS core under the effect of a redox initiation system at ambient.
为了合成表面含磺酸基的双亲型核-壳聚合物,本文采用两步乳液聚合法,第1步合成PS种子乳液;第2步用氧化还原引发体系在PS种子乳胶粒外包覆1层交联的聚苯乙烯磺酸酯,得到表面含磺酸酯的核-壳型聚苯乙烯(CPS)乳胶粒子。
3.
With cassava starch and acrylamide as raw materials,the cassava starch and acrylamide graft copolymerization were synthesized under the condition of redox initiation system.
以木薯淀粉和丙烯酰胺为原料,采用氧化还原引发体系合成淀粉-丙烯酰胺接枝共聚物,研究了温度、引发剂浓度、单体浓度以及反应时间对聚合反应的影响。
2) redox initiator
氧化还原引发体系
1.
The problem of using thermal decomposition initiator in concentrated emulsion polymerization was also pointed out as well as the reason of using redox initiator.
还简单介绍了氧化还原引发体系的分类,回顾了前人在超浓乳液聚合工作中不同单体体系使用的氧化还原引发剂的情况,总结了不同单体体系中氧化剂还原剂的最佳配比,以及它们对动力学、相对分子质量的影响。
2.
The emulsion copolymerization of acrylonitrile and ethylacrylate with a redox initiator system potassium persulfate/sodium bisulfite at low temperature was researched.
用氧化还原引发体系在低温下研究了丙烯腈与丙烯酸乙酯的乳液共聚合。
3) redox initiators
氧化还原引发体系
1.
In this paper,the influences of amounts of redox initiators on polymerization rate,monomer conversion and were discussded.
研究发现:适宜的氧化还原引发体系的用量在单体的0。
4) redox initiator system
氧化还原引发体系
1.
With ammonium persulfate/sodium thiosulfate as Redox initiator system,a binder based on vinyl acetate/acrylate copolymer used for chopped strand mat was prepared at low temperature.
以过硫酸铵/硫代硫酸钠为氧化还原引发体系,在低温下研究制备出了短切毡用的醋酸乙烯酯与丙烯酸酯类共聚物粘结剂。
5) redox initiation system
氧化-还原引发体系
1.
Using N,N,N′,N′-tetramethylethylenediamine and potassium persulphate as a redox initiation system,high molecular weight poly(vinyl acetate)(PVAc) was synthesized by aqueous deposited polymerization.
以N,N,N,′N′-四甲基乙二胺-过硫酸钾为氧化-还原引发体系,用水相沉淀聚合法合成了超高相对分子质量的聚醋酸乙烯(PVAc)。
6) redox system
氧化-还原引发体系
1.
Based on the formula of general VAE emulsion,by adjusting the amounts of colloids and using new redox system,we produced an new kind of VAE with high solid content(65%) and low viscosity, the new VAE has excellent adhesion and fast drying speed.
通过在普通型VAE乳液配方基础上调整保护胶体的品种和用量,并采用新型氧化-还原引发体系,生产出高固含(6S%)低粘度的VAE乳液,具有优异的粘接强度和干燥速度。
补充资料：氧化还原引发体系
分子式：
CAS号：
性质：具有氧化性与还原性的两组分通过氧化还原反应产生自由基，从而引发单体聚合，这样的引发剂是双组分的，称为氧化还原引发剂或氧化还原引发系统。可分为水溶性的和油溶性的。水溶性的氧化剂有过氧化氢、过硫酸铵或过硫酸钾等，相应的还原剂有二价铁离子、亚硫酸钠等。油溶性的氧化剂是有机过氧化物，如过氧化环己酮、过氧化甲乙酮、过氧化二苯甲酰等，用的还原剂是环烷酸盐(钴、锰、钒、铁等)或叔胺类化合物，如N,N-二甲基苯胺、N,N-二乙基苯胺以及硫醇等。氧化还原引发系统的优点是引发聚合速度快，可以在较低温度下引发聚合。
CAS号：
性质：具有氧化性与还原性的两组分通过氧化还原反应产生自由基，从而引发单体聚合，这样的引发剂是双组分的，称为氧化还原引发剂或氧化还原引发系统。可分为水溶性的和油溶性的。水溶性的氧化剂有过氧化氢、过硫酸铵或过硫酸钾等，相应的还原剂有二价铁离子、亚硫酸钠等。油溶性的氧化剂是有机过氧化物，如过氧化环己酮、过氧化甲乙酮、过氧化二苯甲酰等，用的还原剂是环烷酸盐(钴、锰、钒、铁等)或叔胺类化合物，如N,N-二甲基苯胺、N,N-二乙基苯胺以及硫醇等。氧化还原引发系统的优点是引发聚合速度快，可以在较低温度下引发聚合。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条