1) polycrystalline zirconium dioxide fibre
多晶二氧化锆纤维
2) zirconia fiber
氧化锆纤维
1.
Strengthened with polysulfone (PS) ultra filtration membrane, the tensile strength of the zirconia fiberseparator material was improved from 102g/cm(width) to 198g/cm(width), the alkali absorption was improved from2cm/min to 4cm/min and the other performances, such as the thickness, porosity and surface resistance, were not af-fected.
以聚砜微孔膜为增强体制备增强的氧化锆纤维隔膜材料,可使布膜的强度由原来的102g/cm(宽)提高到现在的198g/cm(宽),吸碱速率由原来的2cm/min提高到现在的4cm/min,而其它的性能如厚度、孔隙率及面电阻等基本不受影响,研制的氧化锆纤维碱性电池隔膜材料基本满足工程化应用的要求。
2.
Process and special capability of zirconia fiber prepared by precursor method are introduced in this paper and the phase transition is also expressed.
氧化锆纤维是一种性能优良的特种无机纤维,耐高温、耐腐蚀、抗氧化,具有广泛的应用前景。
3) alumina fiber
多晶氧化铝纤维
4) ZrO 2 crystallization
二氧化锆的晶化
5) zirconia cloth
氧化锆纤维布
1.
Strength of zirconia cloth is effected by several factors.
氧化锆纤维布的强度受到多种因素的影响,当氧化锆纤维布的晶相为四方晶相时,其力学性能最佳;优化布的织物结构可以大幅度提高其强度;PSU和S-PSU对氧化锆纤维布起到增强的作用,PSU也导致其吸碱率和吸碱速率下降,而采用S-PSU代替PSU则对吸碱率和吸碱速率下降会有所改善;通过细化氧化锆晶粒尺寸、提高晶体的完整性、保留气孔结构等方法可以获得高强度的氧化锆纤维布。
6) zirconia fiber products
氧化锆纤维制品
补充资料：氧化锆纤维
分子式：
CAS号：
性质：高ZrO2含量的高熔点多晶纤维。直径4～6μm，密度5.6～5.9g/cm3。氧化锆含量99.6％。熔点2593℃。强度350～700MPa。模量126～154GPa。高温抗氧性好，导热系数低，化学稳定。制法：(1)挤压法，将氧化锆胶体或粒子靠增稠剂挤压成细丝，再烧结成纤；(2)溶液纺丝：将锆盐溶液纺成凝胶纤维，热处理和煅烧后制成纤维；(3)浸渍法，将黏胶丝或其织物浸泡于锆盐溶液中，再热解和煅烧而得；(4)采用类似氧化铝纤维的制法制取氧化锆纤维。用作耐烧蚀隔热功能复合材料及结构复合材料增强剂、燃料电池部件等。
CAS号：
性质：高ZrO2含量的高熔点多晶纤维。直径4～6μm，密度5.6～5.9g/cm3。氧化锆含量99.6％。熔点2593℃。强度350～700MPa。模量126～154GPa。高温抗氧性好，导热系数低，化学稳定。制法：(1)挤压法，将氧化锆胶体或粒子靠增稠剂挤压成细丝，再烧结成纤；(2)溶液纺丝：将锆盐溶液纺成凝胶纤维，热处理和煅烧后制成纤维；(3)浸渍法，将黏胶丝或其织物浸泡于锆盐溶液中，再热解和煅烧而得；(4)采用类似氧化铝纤维的制法制取氧化锆纤维。用作耐烧蚀隔热功能复合材料及结构复合材料增强剂、燃料电池部件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条