1) low-oriented yarn
低取向丝
2) low orientaition yarn,LOY
低取向丝<纺>
3) pre-oriented yarn
预取向丝
1.
The three-color Wulong PET filament of 385 dtex/120 f was prepared from normal PET pre-oriented yarn (POY), cation dyeable PET POY and black PET POY.
以常规涤纶预取向丝(POY)、阳离子染料可染涤纶POY、黑色涤纶POY为原料,生产385 dtex/120 f涤纶三舞龙丝,探讨了其假捻变形的生产工艺。
2.
The trial-production of 35 dtex/24 f fine denier polyester pre-oriented yarn with existing production equipment was introduced.
在公司现有的生产设备上试生产35dtex/24f细旦涤纶预取向丝(POY),研究了聚酯切片含水率、熔体温度、冷却吹风风速、卷绕速度等工艺条件对POY物理性能和条干不匀率的影响。
3.
The structure and mechanical properties of PA6 pre-oriented yarn (POY) and draw textured yarn (DTY) were measured and analyzed.
对PA6预取向丝(POY)和弹力丝(DTY)的结构、力学性能等进行测试分析,探讨了PA6 POY在DTY加工过程中结构的变化对染色性能的影响。
4) partially oriented yarn
预取向丝
5) preoriented yarn
预取向丝
6) POY
预取向丝
1.
Discussion on Production Process of 120dtex/144f PET POY by Direct Spinning;
120dtex/144f涤纶直纺预取向丝生产工艺探讨
2.
Structural Performance of PTT POY and its Post-processing;
PTT预取向丝的结构性能及其后加工
3.
PROCESS TEST OF 82DTEX/68F POY;
82dtex／68f预取向丝的工艺调试
补充资料：高取向丝
分子式：
CAS号：
性质：又称全取向丝。由超高速熔体纺丝制得高取向卷绕丝。纤维取向度高，染色性好，不匀率低、卷装大。纺丝卷绕速度为5500～6000m/min，甚至高达7000～8000m/min。即在高张力下纺丝，使纺丝拉伸加大，导致纤维高度取向。但由于结晶粒子较大，非晶区取向不完善，存在内应力，使纤维断裂伸长较大(40％左右)。不能满足服用纤维要求，不能直接用于纺织加工。若经补充后拉伸或在纺丝卷绕前经热定型，可用于加工仿丝绸织物和变形丝。
CAS号：
性质：又称全取向丝。由超高速熔体纺丝制得高取向卷绕丝。纤维取向度高，染色性好，不匀率低、卷装大。纺丝卷绕速度为5500～6000m/min，甚至高达7000～8000m/min。即在高张力下纺丝，使纺丝拉伸加大，导致纤维高度取向。但由于结晶粒子较大，非晶区取向不完善，存在内应力，使纤维断裂伸长较大(40％左右)。不能满足服用纤维要求，不能直接用于纺织加工。若经补充后拉伸或在纺丝卷绕前经热定型，可用于加工仿丝绸织物和变形丝。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。