The effect of the temperature on the size of austenite grain and the rule of structure inheritance of 10Ni5CrMoV steel was investigated.
结果表明 :奥氏体化晶粒急剧粗化的临界温度为 12 0 0℃ ;奥氏体自发再结晶的最低温度为 85 0℃ ;90 0℃以下奥氏体自发再结晶以形成针状奥氏体和球状奥氏体两种方式进行 ;二次加热时 ,加热温度低于 90 0℃时都有组织遗传发生。
2.
The tendency of structure inheritance of 945 steel was investigated with heat-treatment process in this paper.
通过热处理实验 ,探讨了 94 5钢组织遗传倾向 ,试验结果表明 ,94 5钢晶粒长大倾向较小 ,为本质细晶粒钢。
3.
For 26Cr2Ni4MoV the mechanism of removing structure inheritance by austenite recrystallization and the effect of heating have been studied.
以大型发电机及汽轮机转子用钢（２６Ｃｒ２Ｎｉ４ＭｏＶ钢）为对象，研究了奥氏体再结晶及其消除组织遗传的原因，以及不同加热制度对奥氏体再结晶消除组织遗传的影响规律。
4) Structure heredity
组织遗传
1.
Eliminating structure heredity of 85Cr2Mn2Mo steel by normalizing at high temperature;
高温正火消除85Cr2Mn2Mo钢组织遗传的研究
2.
Effects of Structure Heredity on Grain Refinement in ZAlSi7Mg1 alloy
利用组织遗传性细化ZAlSi7Mg1合金晶粒
3.
The results show that microstructure of laser cladding layer is more fine than that of plasma transferred arc layer,and metallurgical bonding is obtained and structure heredity is observed between the two layers.
结果表明,在等离子喷焊层基体上生长起来的激光熔覆层的组织更加细小,两层之间呈冶金结合,具有明显的组织遗传性。
5) structural inheritance
组织遗传
1.
Elimination process of structural inheritance in Nb-microalloyed steel with CFB/M multiphase structure
Nb微合金化CFB/M复相钢组织遗传的消除工艺
2.
The studies show that mixed grain is caused by structural inheritance.
研究表明 ,混晶是组织遗传造成的 ,调质处理前进行退火处理 ,可获得较为平衡的组织状态 ,从而抑制组织遗传 ,消除混晶和粗晶组织。
3.
This was due to the structural inheritance occurred in laser speediness heating processing.
4Cr13钢淬火态试样激光淬火后晶粒尺寸保持常规淬火水平 ,是快速加热组织遗传造成的结果。
6) structural heredity
组织遗传
1.
In this paper,the rule of structural heredity in Nb-microalloyed CFB/M steel was investigated by experiments.
为细化Nb微合金化CFB/M复相钢的原奥氏体晶粒,对其组织遗传规律进行了实验研究,发现对Nb微合金化CFB/M复相钢进行等温退火与完全退火处理均能有效切断组织遗传,另外,研究发现Nb微合金化CFB/M复相钢在相当宽的加热速率范围内存在组织遗传现象,当加热速度提高到40℃/s以上时不再出现,晶粒开始细化。
2.
The result shows diffusion transformation can occur and can erase the orientation relationship of martensitic structure after isothermal treatment and annealing so as to effectively cut off the structural heredity for Nb-microalloyed CFB/M complex phase steel.
对Nb微合金化CFB/M复相钢的组织遗传规律进行了试验研究。