1) titanium-beryllium
钛铍合金
2) titanium-beryllium
钛铍合金<冶>
3) beryllium gold
铍金合金
4) Be-Al alloy
铍铝合金
1.
Finite element simulation of tensile properties in powder metallurgy Be-Al alloy
粉末冶金铍铝合金拉伸性能的有限元模拟
2.
The results show that Be-Al alloy has satisfying tensile properties at room temperature and the tensile behaviors are sensitive to the strain speed.
通过室温拉伸试验和SEM原位疲劳测试,研究了金属型复合材料铍铝合金的拉伸性能及拉伸和原位疲劳的断裂机制。
3.
The effect of different content of beryllium and aluminum on the microstructure,mechanical properties of the powder metallurgy Be-Al alloy was studied by means of mechanical tensile test at room temperature and SEM analysis.
通过室温拉伸试验和扫描电镜观察与分析,研究不同铍铝配比对粉末冶金铍铝合金的显微组织和力学性能的影响。
5) beryllium copper alloy
铍铜合金
1.
Devolepment of beryllium copper alloy's melting-casting techniques and equipment;
铍铜合金熔铸工艺及设备的发展
2.
A new kind of long life electrode material was developed using beryllium copper alloy.
本项目采用含铍多元铜合金 ,利用含铍铜合金具有较高的硬度、耐高温性能、强度和导电率的综合性能 ,研制出一种达到进口电极性能要求的长寿命新型电极材料 ,通过在进口及国产设备使用完全满足要求 ,解决了国产焊接电极长期存在的焊接质量差、寿命短的问
3.
Rare earth was applied successfully to beryllium copper alloy in our laboratory.
通过本文的工艺研究及试验 ,使稀土成功地应用于铍铜合金中 ,铸锭由于其工艺特点而常出现的气孔、夹杂等缺陷得到了控制 ,同时大大提高了合金的综合性能。
补充资料：铍钛复合材料
分子式： Be/Ti
CAS号：
性质：由钛合金和铍丝组成的复合材料。主要利用钛合金的抗冲能力和铍的高模量、低密度的综合性能。材料的比例级限为137～275MPa，抗拉强度755～1160MPa，伸长率1%～3%，模量123～247GPa。采用金属压力加工工艺生产。用于飞机发动机。
CAS号：
性质：由钛合金和铍丝组成的复合材料。主要利用钛合金的抗冲能力和铍的高模量、低密度的综合性能。材料的比例级限为137～275MPa，抗拉强度755～1160MPa，伸长率1%～3%，模量123～247GPa。采用金属压力加工工艺生产。用于飞机发动机。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。