1) double oriented silicon steel
双取向硅钢板
4) Cubex
库贝克斯双取向硅钢薄板
5) oriented silicon steel
取向硅钢
1.
Effect of Si_3N_4 tensile coating on performance of oriented silicon steel;
氮化硅张力涂层对取向硅钢性能的影响
2.
Effect of tensile coatings through electrodeposition on properties of oriented silicon steel;
电沉积涂层对取向硅钢性能的影响
3.
Influence of nitriding modes and ammonia on nitrogen content of oriented silicon steel
渗氮方式及氨气对取向硅钢氮含量的影响
6) grain-oriented silicon steel
取向硅钢
1.
For preventing the edge cracking produced in hot-rolling grain-oriented silicon steel,some measures are adopted: controlling oxygen concentrate and hold time in atmosphere when slab heating above 1 200℃,adjusting reduction and rolling temperature of roughing mill,carrying out width reduction and brink heating,changing de-formation energy of material and inhibiting brink fish scale-type defect.
川崎取向硅钢存在热轧板边裂问题。
2.
The calculation of single crystal magnetic induction coefficients from measured texture and magnetic induction data in a grain-oriented silicon steel strip has been discussed.
对由取向硅钢薄带的磁感和织构实测数据计算其单晶磁感系数进行了探讨。
补充资料:硅钢
硅钢 silicon steel 含硅量0.5%~4.8%的铁硅合金。是电工领域广泛使用的一种软磁材料。电工用硅钢常轧制成标准尺寸的大张板材或带材使用,俗称硅钢片,广泛用于电动机、发电机、变压器、电磁机构、继电器电子器件及测量仪表中。 硅是钢的良好脱氧剂,它与氧结合,使氧转变为稳定的不为碳还原的SiO2,避免了因氧原子掺杂而使铁的晶格畸变。硅在α铁中成为固溶体后使电阻率增加,同时有助于将有害杂质碳分离出来。因此,一般含杂质的铁加入硅后能提高磁导率、降低矫顽力和铁损。但含硅量增加又会使材料变硬变脆,导热性和韧性下降,对散热和机械加工不利,故一般硅钢片的含硅量不超过4.5%。 硅钢片分冷轧、热轧两种,使用较多的是冷轧硅钢片。冷轧硅钢片沿轧制方向有优良的磁性能,不仅在强磁场中具有高饱和磁通密度和低铁损,而且在弱磁场中也有良好的磁性(初始磁导率大)。这是由于冷轧工艺过程使钢片中杂质含量降低,并在钢片中造成粗大晶粒,致使磁导率增大,磁滞损耗减小。 |
说明:补充资料仅用于学习参考,请勿用于其它任何用途。