1) dynamic creep
动力蠕变
2) creep
[英][kri:p] [美][krip]
蠕变，蠕动，蠕流
3) creep resistance
蠕变抗力
1.
The creep resistance of the alloy increases with the number of second phase precipitates (such as carbide particles and a precipitation) uniformly distribu.
结果表明:位错环组是合金蠕变变形结构中的典型位错组态;合金的蠕变抗力随β基体上弥散分布的第二相析出数量的增加而提高。
2.
The results show that the minimum creep rate of the alloy decreases by two to ten times, creep stress increases by 50 MPa～150 MPa, such an excellent creep resistance results from solution strengthening of high niobium alloying and precipitate strengthening of carbide
2 B合金最小蠕变速率降低 2倍～ 10倍 ,蠕变应力提高 5 0 MPa～ 15 0 MPa,如此优越蠕变抗力主要来自于高铌合金化对钛铝合金的固溶强化及间隙原子的沉淀强
3.
The main reason for the better creep resistance of the alloy, containing more elements Ta and Al, during st.
结果表明 :在 1 0 0 0℃和 1 2 0MPa条件下 ,两合金位错运动的内摩擦力值相近 ,随温度的升高 ,两合金的内摩擦力差值增大 ;随着温度的提高 ,不含Ta的合金中γ′相尺寸和体积分数明显减少 ,而Al和Ta元素含量较高的合金中 ,γ′相保持较高的体积分数是合金蠕变抗力明显提高的主要原因。
4) creep stress
蠕变应力
1.
How to estimate creep stress from small punch creep test results was described in present paper.
主要阐述根据小冲杆试样实测中心挠度求蠕变应力的问题。
5) resistant stress
蠕变阻力
1.
On the basis of reviewing briefly the particle hardening theories and various dislocation creep theories, a modified dislocation creep model was proposed, in which the resistant stress is a key factor to creep mechanism.
在对颗粒强化理论和位错蠕变理论进行回顾、评价基础上,发展了一个位错蠕变阻力模型,认为蠕变阻力是影响铸造镍基高温合金蠕变机制的重要因素。
6) thermal creep
热力蠕变
补充资料：蠕变
| 蠕变 creep 固体材料在保持应力不变的情况下，应变随时间缓慢增长的现象。金属、高分子材料和岩石等在一定条件下都具有蠕变性质。蠕变材料的瞬时应力状态不仅与瞬时变形有关，而且与该瞬时以前的变形过程有关。瞬时响应后随时间发展的蠕变一般可分成 3个阶段：第一阶段是衰减蠕变，应变率（应变的时间变化率）随时间增加而逐渐减小；第二阶段是定常蠕变，应变率近似为常值；第三阶段是加速蠕变，应变率随时间逐渐增加，最后导致蠕变断裂。同一材料在不同的应力水平或不同温度下，可处在不同的蠕变阶段。通常温度升高或应力增大会使蠕变加快。不同材料的蠕变微观机制不同。引起多晶体材料蠕变的原因是原子晶间位错引起的点阵滑移以及晶界扩散等；而聚合物的蠕变机理则是高聚物分子在外力长时间作用下发生的构形和位移变化。研究材料的蠕变性质对安全而经济地设计结构和机械零件具有重要意义。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。