1) creep internal stress
蠕变内应力
1.
The research was carried out on the basis of CSR to measure creep internal stress.
采用CSR法对蠕变内应力的测试进行了研究,并在材料试验机上实现了CSR法的蠕变内应力测试。
2.
In this paper,measuring method of creep internal stress are studied.
对蠕变内应力的测试方法进行研究。
3.
It is also shown that under the creep limit failure criterion, the creep internal stress method has the advantage of less test time in comparison with the isothermal .
用恒应变速率法测定高温管道蠕变内应力并预测其残余寿命,不管是以蠕变极限为失效准则,还是以持久强度为失效准则,都可获得令人满意的结果;而以蠕变极限为失效准则的蠕变内应力法与常规的以蠕变试验为基础的等温外推法相比,还具有试验时间短的优点。
2) creep stress
蠕变应力
1.
How to estimate creep stress from small punch creep test results was described in present paper.
主要阐述根据小冲杆试样实测中心挠度求蠕变应力的问题。
3) creep under variable stress
变应力蠕变
4) hoek-brown rule
预应力蠕变
5) high stress creep
高应力蠕变
6) stress creep rate
应力蠕变率
补充资料：淬火内应力
淬火内应力
intra-stress from quenching
应力与热应力相反的推断。 纵向应力切向应力径向应为 SOOr一一，---下一一---，r一-----r一一-一-，r~一一一一，r，---一门 400卜-一，一月一一~一训班盗一一于+一一场洲卜一—一卜一一一 口州111川l轰.月川11川川11人.，l川川1 11 岁olujlUJ与而而，1沪翅JJI洲坦“、t口n书1111沪1山刀{陌丽而而击丽而侧 只!胡lllllly}l划11详l!、咐}}川少尸l 一400卜一一一~平一-一月卜一一-一仁一一-一}一一一‘仁一一州 一800L‘eseseswei-weeseswe口L‘es-J-‘一‘一目L-一一-J.一习 圆心四回心回阅·心回 截面位置 图3棒状工件的淬火组织应力 (Fe一16 Ni，小50mm汤爪300℃， 加热奥氏体化后缓冷至300℃， 整体浸入冰水冷至。℃， 室温测定应力) (陈景榕)干二一二一罗二斋 }}}}{}l}}}}{}}}川}川} a卜- 侧}、，l、、钊‘_ 几几几勺 时间: b。‘…广粉火…厂 只陈万一一一一节一，一一一，二洲冬 ‘…”卜份杯间丁丫详 图1棒状工件不均匀淬冷时的轴向热应力 a一棒状工件轴向淬冷内应力研究的最简化模型; b一r、皿两部分的降温曲线; 。一热应力随时间的变化曲线 检测实例图2、图3分别是对中等尺寸的短棒状工件经整体浸入冷却介质激冷(到。℃)，热应力和组织应力的实测结果。为了获得单一的热应力或组织应力，设计了特殊的加热、冷却工艺，如图题后括号中的说明。试件在浸冷时，外圈可参考图1份中的;，心部则相当于工。热应力测定结果与图1c(介)相一致。运用相似的推理，不难理解切向和径向的残留热应力形成机制。