1) boron nitride coating
氮化硼涂层
2) Boron carbide coating
碳化硼涂层
1.
The microstructure and phases composition of the boron carbide coating were investigated using SEM, EDS and X-Ray diffraction.
利用自制的电磁加速等离子喷涂装置在45钢基体上制备了碳化硼涂层,运用扫描电镜、能谱分析及X射线衍射分析对碳化硼涂层的形貌和相组成进行了定性的分析。
2.
Thermal shock behavior of plasma sprayed boron carbide coatings was studied.
研究了等离子喷涂碳化硼涂层在不同能量密度的激光辐照下的耐热冲击与热蚀行为。
3.
Boron carbide coatings were deposited via vacuum plasma spraying, and then their microstructure, phase composition, hardness and bonding strength were examined.
本文采用真空等离子喷涂方法制备碳化硼涂层,对涂层的结构、组成、硬度及结合强度进行了观察与测定。
3) HfB 2 coating
硼化铪涂层
1.
Through processing their load-displacement curves, the elastic modulus of HfB 2 coating was obtained,whose value is 188.
通过对测得的载荷—位移曲线进行处理 ,得到硼化铪涂层的弹性模量为 188 78GPa。
4) turbostractic boron nitride
湍层氮化硼
5) C_3N_4-film
氮化碳涂层
1.
Research on Si-rich Si-Al alloy cutting by the cutting tool coated by diamond film or C_3N_4-film;
金刚石和氮化碳涂层刀具加工高硅铝合金
6) TiN film
氮化钛涂层
1.
The paper recommended some new technology of colating TiN films,e.
介绍了几种沉积氮化钛涂层的新技术。
2.
The effect of application of magnetic control or not on are source,mitrogen partial pressure, bias voltage and temperature of substrate when TiN coating is formed on microstructure and properties of TiN films are investigated.
在研制的大弧源多弧离子镀膜机内进行了沉积氮化钛工艺试验，研究了弧源施加磁控与否、氮分压、基板偏压和形成氮化钛时工件温度等工艺参数，对氮化钛涂层微观组织和性能的影响。
补充资料：碳化硼纤维
分子式：
CAS号：
性质：实为以钨丝为芯、碳化硼为皮层的陶瓷纤维。直径多为100μm，密度2.63g/cm3，强度2.68GPa，初始模量412GPa，在2200℃下强度只略有下降。制法主要采用化学气相成长法，在1200℃以上将三氯化硼、氢和甲烷混合物通人反应室，使反应产物B4C沉积在直径15μm的移动钨丝上而得。用途是作复合材料增强剂等。
CAS号：
性质：实为以钨丝为芯、碳化硼为皮层的陶瓷纤维。直径多为100μm，密度2.63g/cm3，强度2.68GPa，初始模量412GPa，在2200℃下强度只略有下降。制法主要采用化学气相成长法，在1200℃以上将三氯化硼、氢和甲烷混合物通人反应室，使反应产物B4C沉积在直径15μm的移动钨丝上而得。用途是作复合材料增强剂等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条